The deformation creep characteristics of as cast silicon particles reinforced zinc based alloys (Si/ZA27) were determined by high temperature creep experiments at 453 K and 61.1 MPa condition. The experimental results indicated that the minimum creep rate of the silicon containing alloys are about three fifth of that of the matrix alloy(ZA27). The deformation process is mainly controlled by grain boundary sliding mechanism. Both dislocation climb and disperse silicon phase are also contributed to it. Micro structural changes were investigated during the deformation experiments.
The deformation creep characteristics of as cast silicon particles reinforced zinc based alloys (Si / ZA27) were determined by high temperature creep experiments at 453 K and 61.1 MPa condition. The experimental results that the minimum creep rate of the silicon containing alloys are about three fifth of that of the matrix alloy (ZA27). The deformation process is mainly controlled by grain boundary sliding mechanism. Both dislocation climb and disperse silicon phase are also contributing to it. Micro structural changes were investigated during the deformation experiments.