【摘 要】
：
在载流高速摩擦磨损试验机上进行磨损试验,研究了速度和电流对输电材料(纯铜)磨损性能的影响,并对摩擦表面形貌进行了观察。结果表明:在一定速度条件下,电流增大,纯铜的摩擦
【机 构】
：
黄河科技学院工学院,新乡职业技术学院机电系,
论文部分内容阅读
在载流高速摩擦磨损试验机上进行磨损试验,研究了速度和电流对输电材料(纯铜)磨损性能的影响,并对摩擦表面形貌进行了观察。结果表明:在一定速度条件下,电流增大,纯铜的摩擦系数减小,磨损率增大;在一定电流条件下,速度增大,纯铜的摩擦系数和磨损率都增大;在电流和速度的影响下,摩擦表面呈现粘着、塑性变形及氧化磨损特征。
The wear test was carried out on a high current friction and wear tester. The effects of velocity and current on the wear properties of the transmission material (pure copper) were studied. The friction surface morphology was also observed. The results show that under certain speed, the current increases, the friction coefficient of pure copper decreases, and the wear rate increases. Under certain current conditions, the friction coefficient and wear rate of pure copper increase when the current increases And the speed of the friction surface showed adhesion, plastic deformation and oxidation wear characteristics.
其他文献
采用等离子喷涂技术在CuCo_2Be合金表面制备Cr_3C_2-NiCr涂层,通过正交试验确定了CuCo_2Be合金表面等离子喷涂的最优工艺,并对在最佳工艺参数下喷涂的试样,选择在500℃进行高
采用钨极氩弧焊(GTAW)打底+手工电弧焊(SMAW)相结合的复合焊接方法对2205双相钢和Q345碳钢复合板进行了焊接处理,研究了E2209、E309和E309Mo焊材对焊接接头组织与性能的影响
研究了在应变速率0.001 s-1条件下,TLM钛合金在室温压缩和850℃热压缩的形变机理和组织演变规律。实验结果表明:TLM钛合金在冷压缩和热压缩条件下具有不同的形变机理和组织演
钛及钛合金具有比强度大、综合性能优越、具有较好的耐腐蚀性、焊接性和一定的耐热性能,广泛应用于航空和石油化工等领域。文章就钛及钛合金的P+T焊接工艺进行研究,形成焊接
内波的波致流为沿水深方向非均匀分布的剪切流,而深海平台立管的自然模态具有低频、密集的特性,这种流场和结构的特点使得深水立管的涡激振动表现出高阶模态、多阶模态参与振
采用红外热像法对循环载荷下AZ31B镁合金电子束焊接接头的疲劳行为进行研究。对试件在疲劳试验中表面温度演变规律和产热机制进行分析,并在此基础上对其疲劳极限进行预测,同
在耐力项目的比赛过程中教练员面对的主要问题有:一如何科学地预测运动员的比赛状态;二是如何及时地对比赛过程进行指挥和监控。这是困扰教练员的最重要的两个问题。达米拉诺
努力促进区域协调发展,打造北部湾经济区升级版,加快珠江-西江经济带发展,大力振兴左右江革命老区,扩大提升桂林国际旅游胜地影响力,加快沿边地区开发开放,积极稳妥推进新型
The geomorphological environment is one of the most fundamental variables af-fecting the development of human society.The mission of geomorphological environmen
The aim of this study was to evaluate the strain hardening and hot deformation behavior of asextruded Mg-Zn-Mn(ZM31) magnesium alloy with varying Y contents(0.3