论文部分内容阅读
A novel nano-TiO2-xNx composite was used as photocatalyst and added to the interior wall paint. The average diameter of nano-TiO2-xNx was about 20 nm. The majority crystal component of the sample was anatase and its optical absorption edge was shifted from 387 nm to 520 nm significantly. Nano-composite paint containing different dosage of nano-TiO2-xNx was investigated to study the properties of formaldehyde decomposition in the air. Testing results show that the formaldehyde decomposition ratio of that nano-paint can almost reach above 80%, especially for that of the paint containing 3% (w/w) nano-TiO2-xNx, which exceeded 90%. The primary investigation on the reaction kinetics of photocatalytic formaldehyde decomposition indicated that the experiment data well fit the model of first-order reaction kinetics.