By testing the melt index (MI), tensile strength and breaking extension ratio, the thermal ageing rate of polyoxymethylene (POM) was analyzed and compared. The
【机 构】
：
College of Chemical Engineering
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
By testing the melt index (MI), tensile strength and breaking extension ratio, the thermal ageing rate of polyoxymethylene (POM) was analyzed and compared. The surface morphology and type of function group of POM surface were observed and analyzed by SEM and XPS. The results show that the MI value increases gradually with the ageing time at 120 ℃, indicating that the thermal oxidation decomposition occurrs slowly. The effect of 20-day thermal ageing on the tensile strength and breaking extension ratio of POM is not obvious, showing that the ageing of POM is quite a long process. After 105-day, thermal ageing cracking and powdering occurr on the POM surface. XPS determination shows the C1s spectra of samples before and after ageing include two peaks of C-C and C-O, while after ageing the content of C-C decreases and the content of C-O increases, indicating that the thermal ageing of POM is mainly the breaking and decomposing of C-C bond. The O1s/C1s ratio of original samples is 56.98% and after 105-day thermal ageing the ratio is 72.92%.
其他文献
一直以来教师的身份缥缈恍惚，有“一日为师，终生为父”，有“灯塔”，有“园丁”有“太阳下最光辉的人”等，社会一直以模糊的概念定义教师，这些概念赋予的意义被人们逐渐淡化时，便难以
Nd2O3 was used to support Al2O3 and ZnO to prepare a supported solid base catalyst and investigate the effect of catalyst and reaction conditions on the synthes
Carbon soot containing fullerene was continuously produced in volume by pyrolyzing acetylene in thermal HF-Plasma. The characteristics of the carbon soot and C6
Copper nanopowders were successfully prepared by anodic arc discharging plasma method with home-made experimental apparatus. The effects of various processing p
In this article, a multiobjective optimization strategy for an industrial naphtha continuous catalytic reforming process that aims to obtain aromatic products i
Uniform droplet formation from capillary stream breakup provides promising opportunities for many applications such as solder balls manufacturing, circuit board
Oxygen deficient Nd0.67Sr0.33MnO3-δ ceramic samples were prepared using conventional ceramic technology. A colossal electroresistance (CER) effect was found in
In this study, nanosized TiO2 co-doped with Fe3+ and Nd3+ ions was synthesized via a sol-gel method. The metallic ion doped TiO2 was thoroughly characterized wi
3-mercaptopropyl trimethoxysilane (MPTS) was prepared on glass substrate so as to form a two-dimensional self-assembled monolayer (SAM), and the terminal -SH gr
Effects of the surfactant for improving the properties of MIM feedstock were investigated. Feedstocks were prepared by 17-4PH stainless steel(SS) powder and par