A method for strengthening damaged tubular steel T-joints under axial compression by wrapping them with carbon fiber-reinforced polymer(CFRP)sheets was proposed and evaluated.The influence of the CFRP strengthening on the failure mode and load capacity of T-joints with different degrees of damage was investigated using experiments and finite element analyses.Five T-joints were physically tested:one bare joint to obtain the peak load and corresponding displacement(Δ1m),two reinforced joints to provide a reference,and two pre-damaged then retrofitted joints to serve as the primary research objects.The ratio of the pre-loaded specimen chord displacement to the value ofΔ1m was considered to be the degree of damage of the two retrofitted joints,and was set to 0.80 and 1.20.The results demonstrate that the maximum capacity of the retrofitted specimen was increased by 0.83％-15.06％over the corresponding unreinforced specimens.However,the capacity of the retrofitted specimen was 2.51％-22.77％lesser compared with that of the directly reinforced specimens.Next,111 numerical analysis models(0.63≤μ≤0.76,9.70≤γ≤16.92)were established to parametrically evaluate the effects of different geometric and strengthening parameters on the load capacity of strengthened tubular T-joints under different degrees of damage.The numerical analysis results revealed that the development of equivalent plastic strain at the selected measuring points was moderated by strengthening with CFRP wrapping,and indicated the optimal CFRP strengthening thickness and wrapping orientation according to tubular T-joint parameters.Finally,reasonable equations for calculating the load capacity of CFRP-strengthened joints were proposed and demonstrated to provide accurate results.The findings of this study can be used to inform improved CFRP strengthening of damaged tubular steel structures.