Compression tests at room and high temperature and creep tests at high temperature have been performed on B2 Nb15Al20V and Nb10Al20V alloys. At room temperature,in the as-cast state, both alloys exhibited significant ductility in compression. The dislocations showed good mobility. Dislocation clusters also triggered the formation of pseudotwins, which resulted in serrated yielding. In steady state creep, deformation occurred by a combination of dislocation glide and climb, giving a homogeneous miphase structure with a few dislocations in the A15 phase but no dislocations in the A2 phase.