【摘 要】
：
The effect of small amount gallium (up to 0.06%) on the corrosion behavior of pure aluminum (99.99%,4N) in chloride solution was investigated using a potentiody
【机 构】
：
上海交通大学金属基复合材料国家重点实验室,The State Key Laboratory of Metal Matrix Composites
论文部分内容阅读
The effect of small amount gallium (up to 0.06%) on the corrosion behavior of pure aluminum (99.99%,4N) in chloride solution was investigated using a potentiodynamic polarization technique.It has been found that the open circuit corrosion potential and the pitting potential shifted in the active (negative) direction with increasing gallium content,while corrosion rate and pitting occurrence factor for aluminum increased.The effect of gallium on the degradation of corrosion resistance is rather small while the gallium content is below 0.03mass%.The gallium content should be kept less than 0.03mass% in the pure aluminum.
其他文献
在丝网印刷碳电极的0.125 mm绝缘带上直接铺展微观孔径为300～400 nm的聚苯胺(PANI)纳米纤维(直径60 nm)薄膜,构建气体传感元件.通过监测甲苯、乙醇及二氯甲烷蒸气对气体传感元
研究了果蝇细胞内生物钟基因调节网络的分子噪声,特别讨论了生物钟系统处于略微远离振荡区域的稳态时分子噪声对于时钟蛋白的日夜节律振荡的影响.结果表明:(1)虽然时钟蛋白合
在1-丁基-3-甲基咪唑硫酸氢盐(BMIHSO_4)离子液体中,采用循环伏安法合成了苯胺和环氧丙烷共聚物(PAN-PPO),并与聚苯胺(PAN)进行了对比。结果表明:在相同条件下,PAN-PPO的电合
以ⅠA族元素钾(K)作为掺杂剂,利用射频磁控溅射沉积技术,在单晶Si(111)衬底上成功生长了K:p-ZnO薄膜.采用Hall测试仪、X射线衍射、原子力显微镜和X射线光电谱等测试分析技术,
制备了结构为铟锡氧化物(ITO)/NPB/插入层/Alq/LiF/Al的有机电致发光(EL)器件,测量了器件发光随电压变化的光谱和电压-电流-亮度特性,观察到这种结构器件在电压升高的过程中
使用密度泛函理论B3LYP和B3P86,以及组态相互作用方法CCSD(T)和QCISD,利用多个基组对7Li2(X1∑g+)分子的平衡核间距(Re)、谐振频率(ωe)和离解能(De)进行了计算,发现在CCSD(T
为了解严和店窑汝瓷和钧官瓷的起源关系,用能量色散Χ射线荧光光谱仪(EDXRF)测量了56个严和店窑汝瓷和钧官瓷样品的主量化学组成.一维和二维散布分析显示钧官瓷胎的原料来源
激光二极管(LD)中心波长及LD功率影响着LD泵浦的固体激光器输出特性,通过理论和实验研究了LD的工作温度变化对LD中心波长及LD功率的影响,分析了LD温度控制系统的温控精度,给
本研究涉及几种自制碳场电子发射体,介绍探索这些碳场电子发射体应用的过程中,在真空电子学、真空微/纳电子学(VMF/VNE)领域内获得成功的方面.研究工作涉及到了一些新开发的
以4,6-二氨基-1,3-苯二酚盐酸盐(DADHB),对苯二甲酸(TA)、1,4-萘二甲酸(1,4-NDA)为原料,在多聚磷酸体系中合成了聚(1,4-亚苯基)苯并双噁唑(PB0)、聚(1,4-亚萘基)苯并双嗯唑(P