Synthesis and Characterization of Mesoporous Europium (Ⅲ) Silicate Molecular Sieves

来源 :稀土学报(英文版) | 被引量 : 0次 | 上传用户:huntout
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The luminescent nanosized Eu-MCM (1:10) was synthesized by means of sol-gel-assisted self-assembly under basic conditions at room temperature. The results of 29Si-MAS NMR show that the peaks are Q4, Q3, Q2 [(SiO)4-mSi-(OH)m (m=0, 1, 2), at -δ111, -δ103, -δ90], and q3, q2, q1, q0 [(SiO)4-nSi-(O-Eu)n (n=1, 2, 3, 4 ), at -δ83, -δ72, -δ55, -δ47]. The result proves Eu3+ doped Si-O framework. The HRTEM image shows that the regular uniform nanoparticles with a diameter of 15 nm possess large pore with Φ8 nm, which is consistent with the result of N2 adsorption. The patterns of selected-area electron diffraction, XRD, and pore-size distribution plot of Eu-MCM (1:10) show that the sample of Eu-MCM (1:10) possesses the both of crystal and amorphous phases. The FT IR results indicate that the peaks near 970 cm-1 are assigned to the deformation vibration of silanol group. The as-product was calcined at 800 ℃ and the mesoporous material possesses enormous specific areas and large pores, which shows that the mesoporous material is ultrastable.
其他文献
The microstructure and mechanical properties of as-cast and as-extruded Mg-Zn-Y alloy (Mg-11%Zn0.9%Y, mass fraction) containing Mg3 YZn6 quasicrystal were studi
NiO buffer layers were formed on a tape of Ni for making YBCO coated conductor by surface-oxidation epitaxy (SOE) process. Different oxidizing conditions such a
Nanocrystalline tungsten carbide thin films were fabricated on graphite substrates by plasma enhanced chemical vapor deposition (PECVD) at H2 and Ar atmosphere,
The effect of size and distribution of titanium carbide on the microstructure and mechanical properties of non-burning β titanium alloy Ti-25V-15Cr-2Al-0.2C-0.
In this work, a thermodynamic model is developed for prediction of structure H hydrate formation. The model combines the Peng-Robinson equation of state for the
The solder joint reliability of a 0. 5 mm lead pitch, 240-pin quad flat package(QFP) was studied by nonlinear finite element analysis(FEA). The stress/strain di
Nanosized orthorhombic LiMnO2 was successfully synthesized using Mn2O3 and LiOH.H2O as starting materials.Not only the reaction temperature was lower, but the r
Indium tin oxide ( ITO ) thin films ( 100 ± 10 nm) were deposited on PC ( polycarbonate ) and glass substrates by rf( radio-frequency ) magnetron sputtering. T
The internal frictions of the specimens in the waist centre of the commercial BNb and BNbRE rails, which were left in air for two years, were measured. It is fo
2007年夏季对青岛沿海石莼科绿藻,包括定生石莼Ulva、定生浒苔Enteromorpha以及漂浮浒苔Enteromorpha进行了样本采集,针对其17种金属元素和3种非金属元素进行了含量分析与比