摘要：本文主要论述高性能混凝土的特性及高性能混凝土原材料选用的技术要求，着重阐述了高性能混凝土关键材料水泥、骨料、外加剂及活性掺合料的技术要求，详实列出了C65高性能混凝土的配合比数据，论述了高性能混凝土在生产与施工中须重视的质量控制措施。
关键词：高性能混凝土活性掺合料混凝土水灰比混凝土坍落度。
liuWenqing
Construction Engineering Co., Ltd. Sichuan Hui Rong Sichuan. Ziyang641300
Abstract:This text is main to discuss the characteristic and the high performance concretes original material of the high performance concrete to choose the technique request for use, emphasizing to elaborate the high performance concrete valve key material cement, bone to anticipate, the in addition and the technique request of the live in addition material, thorough listed the data of mix proportion of the C65 high performance concrete, discuss the high performance concrete at produce to control the performance with the mass that under construction beard value.
Key word:The high performance concrete, live in addition material, concrete water cement ratio, concrete collapses to fall the degree.
1、工程簡介
深圳茂业时代广场是一座超高层建筑，工程位于深圳市南山区文心二路侧，南侧为海德二道，西边是南山书城。建筑总高度：127.5m,总建筑面积: 90065.62m2。地下室：3层，塔楼：24层,裙楼：9层,塔楼为钢框架筒结构，底层柱截面为:1.5m*1.5m钢筋混凝土柱、核心筒部分柱子与核心筒转角部分增加H型钢钢结构骨架，外包高强混凝土。塔楼9层以下柱、核心筒墙混凝土设计强度等级为C65，该工程的技术难点之一是柱、墙C65高性能混凝土的配制与施工。
2、高性能混凝土的特性
高性能混凝土是在大幅度提高常规混凝土性能基础上，采用现代混凝土技术，通过优选原材料并在混凝土中加入足够数量的活性掺和料和高性能外加剂的一种新型高技术混凝土。它具有高强度、高耐久性和优良的工作性三个特点。由于以上特性，高性能混凝土在现代高层建筑中得到广泛应用，并极大地促进了现代超高层建筑的发展。
3、高性能混凝土原材料技术性能要求
3.1水泥:水泥在混凝土中起着凝结作用，水泥标号高低、质量优劣对高性能混凝土的特性有极大影响。常规下,高性能混凝土须使用525号以上普通硅酸盐水泥或中热硅酸盐水泥。根据本工程的情况,工程择优选择了福建“顺昌”PO.525炼石水泥作为C65高性能混凝土原材料，检验资料显示:炼石P.O525水泥28天平均强度为:62Mpa，该水泥矿物成分C3A含量低,质量稳定,适宜配制高性能混凝土。该水泥主要矿物成份:C3S为40-55%,C2S为20-30%,C3A为6-8%,C4AF为10.5-12.5%,R2O为0.4-0.6%。水泥的各项技术性能指标符合配制高性能混凝土要求，其技术性能指标见表1
表1 P.O525炼石水泥技术性能指标
检验项目 凝结时间
(min) 抗折强度
(Mpa) 抗压强度
(Mpa) 细度
(%) 安定性雷氏法
(mm) SO3含量
(%) 烧失量
(%)
初凝 终凝 3d 28d 3d 28d
检验结果 96 160 6.2 9.1 36.6 66.6 1.9 1.0 1.89 2.49
3.2河沙:高性能混凝土用砂要严格控制含泥量和有害杂质，沙的含泥量不得超过3%，云母、轻物质、硫化物、及硫酸盐含量不得大于1%。要合理调整砂率，细度模数应在2.8以上，为保证高性能混凝土的可泵性，0.63mm粒径砂的累计筛余应控制在70%-75%。本工程C65高性能混凝土采用了福建龙海出产的河沙, 中砂,其细度模数为：2.9,含泥量0.9%,表观密度:2590kg/m,堆积密度:1460kg/m3,紧密密度:1650kg/m3。其杂质含量及沙颗粒级配符合要求。颗粒级配见表2
表2砂颗粒级配
筛孔尺寸(mm) 5.00 2.50 1.25 0.63 0.315 0. 16
累计筛余(%) 1 12 23 52 82 99
3.3碎石:高性能混凝土对粗骨料要求高，粗骨料须质地坚硬。粗骨料坚硬程度直接影响高性能混凝土的强度。配制高性能混凝土的粗骨料与普通混凝土的要求不同,除要求骨料质地坚硬外，还必须选用级配良好的石料，C60以上高性能混凝土骨料最大粒径一般不超过25mm，粒径应在5-25mm连续级配。本工程C65混凝土骨料选用厦门市海沧产"金路桥"花冈石碎石,其表观密度:2660 kg/m3，堆积密度:1480 kg/m3，紧密密度:1660 kg/m3，针片状含量:4.4%,压碎指标:6.2,含泥量:0.5%，其各项技术指标符合配制高性能混凝土要求。碎石级配见表3
表3碎石级配
筛孔尺寸(mm) 25.00 20.00 16.00 10.00 5.00 2.50
累计筛余(%) 2 24 55 95 99 100
3.4粉煤灰:粉煤灰具有以下基本效应:形态效应,活性效应的微集料效应，粉煤灰混凝土与等强度的普通混凝土相比,其性能在拌制、施工、硬化过程中都发生了很大变化。这种变化提高了混凝土的工作性即流动性、粘聚性、保水性，降低了混凝土硬化阶段的水化热，提高了混凝土强度，也提高了混凝土的抗渗性、抗侵蚀性、耐磨性等耐久性能。由于粉煤灰对混凝土的各项性能影响大，因此，其参量及本身质量一定要严格控制。本工程C65混凝土选用的是厦门嵩屿火电厂生产的I及粉煤灰，该粉煤灰细度(45um)筛余9.5%,需水量比:92%,烧失量3.72%,含水量0.5%三氧化硫含量:1.98%。其各项技术指标符合配制高性能混凝土要求。
3.5外加剂：高性能混凝土所用外加剂要满足在低水灰比条件下提高混凝土流动性的要求，所以外加剂的性能质量至关重要。为此，本工程C65高性能混凝土选用了质量可靠，性能稳定的萘系FDN高效缓凝减水剂，其各项技术指标为：密度:1.168g/ml,含固量:32.74%,PH值:6.4,砂浆减水率:19.1%，技术指标符合要求。
4.C65高性能混凝土配合比
本工程C65高性能混凝土配合比經实验室试配完成后，高性能混凝土试块经试压其28天强度均达到设计要求，配合比满足现场施工要求。C65高性能混凝土配合比结果见表4
表4 C65混凝土试验配合比:
混凝土配合比 水灰比
砂率
(%) 水泥
(kg) 水
(kg) 砂
(kg) 石
(kg) 掺合料(kg) 外加剂
(kg)
混凝土试验配合比 0.28 38 449 145 639 1039 135 16.4
5.C65高性能混凝土生产质量控制
5.1.1原材料的储存和标识
高性能混凝土专用原材料必须分厂家、品种、规格、等级存放，由于原材料的特殊重要性，须将其堆放点与其它原材料隔离，不得混仓，并作好标识，进料必须保证原材料的相对稳定。
5.1.2高性能混凝土生产前原材料的检查
高性能混凝土生产前应将生产备料做一次适应性试验，检查生产用料与其试配用原材料有无不同，如有明显差别，须从新备料。
5.1.3高性能混凝土的计量、搅拌与运输
计量混凝土原材料用的仪器、仪表，计量原材料前必须进行校准，计量精度：水泥、粉煤灰、外加剂小于+1%，砂石小于+2%，须充分保证原材料计量精度及混凝土配合比正确无误。高性能混凝土的运输要实行专车专用，在运输中混凝土运输车滚筒必须慢速正转，以避免高性能混凝土发生离析。施工中不得随意向混凝土中加水，搅拌车卸料前滚筒须先快速转动一分钟，使混凝土搅拌均匀后再卸料入泵。
6.高性能混凝土施工质量控制
高性能混凝土在施工中其可泵性不如普通混凝土，为防止混凝土堵管，保证高性能混凝土的连续施工，高性能混凝土的坍落度宜控制在200+20mm范围内。高性能混凝土在施工过程中其前期强度增长较快，若混凝土养护工作滞后或不及时高性能混凝土易产生裂缝，影响工程质量。施工中为确保高性能混凝土养护质量，可在构件较难养护的侧面紧贴挂湿润的麻袋进行覆盖养护，混凝土拆模后应及时涂刷养护剂,保证高性能混凝土得到充分养护。
7.结论
本工程 柱、墙C65混凝土浇筑完成后,按规定对C65高性能混凝土进行了现场见证试块取样，试块经广东省深圳市建筑材料检测中心试压检测,其28天抗压强度值均达到设计强度。C65高性能混凝土施工质量达到了设计、规范要求。
参考文献
1、《混凝土质量控制标准》GB50164-2002 2、《混凝土结构工程施工质量验收规范》GB50204—2002
3、《高层建筑混凝土结构技术规范》JGJ 3-2002
注：文章内所有公式及图表请以PDF形式查看。
关键词：高性能混凝土活性掺合料混凝土水灰比混凝土坍落度。
liuWenqing
Construction Engineering Co., Ltd. Sichuan Hui Rong Sichuan. Ziyang641300
Abstract:This text is main to discuss the characteristic and the high performance concretes original material of the high performance concrete to choose the technique request for use, emphasizing to elaborate the high performance concrete valve key material cement, bone to anticipate, the in addition and the technique request of the live in addition material, thorough listed the data of mix proportion of the C65 high performance concrete, discuss the high performance concrete at produce to control the performance with the mass that under construction beard value.
Key word:The high performance concrete, live in addition material, concrete water cement ratio, concrete collapses to fall the degree.
1、工程簡介
深圳茂业时代广场是一座超高层建筑，工程位于深圳市南山区文心二路侧，南侧为海德二道，西边是南山书城。建筑总高度：127.5m,总建筑面积: 90065.62m2。地下室：3层，塔楼：24层,裙楼：9层,塔楼为钢框架筒结构，底层柱截面为:1.5m*1.5m钢筋混凝土柱、核心筒部分柱子与核心筒转角部分增加H型钢钢结构骨架，外包高强混凝土。塔楼9层以下柱、核心筒墙混凝土设计强度等级为C65，该工程的技术难点之一是柱、墙C65高性能混凝土的配制与施工。
2、高性能混凝土的特性
高性能混凝土是在大幅度提高常规混凝土性能基础上，采用现代混凝土技术，通过优选原材料并在混凝土中加入足够数量的活性掺和料和高性能外加剂的一种新型高技术混凝土。它具有高强度、高耐久性和优良的工作性三个特点。由于以上特性，高性能混凝土在现代高层建筑中得到广泛应用，并极大地促进了现代超高层建筑的发展。
3、高性能混凝土原材料技术性能要求
3.1水泥:水泥在混凝土中起着凝结作用，水泥标号高低、质量优劣对高性能混凝土的特性有极大影响。常规下,高性能混凝土须使用525号以上普通硅酸盐水泥或中热硅酸盐水泥。根据本工程的情况,工程择优选择了福建“顺昌”PO.525炼石水泥作为C65高性能混凝土原材料，检验资料显示:炼石P.O525水泥28天平均强度为:62Mpa，该水泥矿物成分C3A含量低,质量稳定,适宜配制高性能混凝土。该水泥主要矿物成份:C3S为40-55%,C2S为20-30%,C3A为6-8%,C4AF为10.5-12.5%,R2O为0.4-0.6%。水泥的各项技术性能指标符合配制高性能混凝土要求，其技术性能指标见表1
表1 P.O525炼石水泥技术性能指标
检验项目 凝结时间
(min) 抗折强度
(Mpa) 抗压强度
(Mpa) 细度
(%) 安定性雷氏法
(mm) SO3含量
(%) 烧失量
(%)
初凝 终凝 3d 28d 3d 28d
检验结果 96 160 6.2 9.1 36.6 66.6 1.9 1.0 1.89 2.49
3.2河沙:高性能混凝土用砂要严格控制含泥量和有害杂质，沙的含泥量不得超过3%，云母、轻物质、硫化物、及硫酸盐含量不得大于1%。要合理调整砂率，细度模数应在2.8以上，为保证高性能混凝土的可泵性，0.63mm粒径砂的累计筛余应控制在70%-75%。本工程C65高性能混凝土采用了福建龙海出产的河沙, 中砂,其细度模数为：2.9,含泥量0.9%,表观密度:2590kg/m,堆积密度:1460kg/m3,紧密密度:1650kg/m3。其杂质含量及沙颗粒级配符合要求。颗粒级配见表2
表2砂颗粒级配
筛孔尺寸(mm) 5.00 2.50 1.25 0.63 0.315 0. 16
累计筛余(%) 1 12 23 52 82 99
3.3碎石:高性能混凝土对粗骨料要求高，粗骨料须质地坚硬。粗骨料坚硬程度直接影响高性能混凝土的强度。配制高性能混凝土的粗骨料与普通混凝土的要求不同,除要求骨料质地坚硬外，还必须选用级配良好的石料，C60以上高性能混凝土骨料最大粒径一般不超过25mm，粒径应在5-25mm连续级配。本工程C65混凝土骨料选用厦门市海沧产"金路桥"花冈石碎石,其表观密度:2660 kg/m3，堆积密度:1480 kg/m3，紧密密度:1660 kg/m3，针片状含量:4.4%,压碎指标:6.2,含泥量:0.5%，其各项技术指标符合配制高性能混凝土要求。碎石级配见表3
表3碎石级配
筛孔尺寸(mm) 25.00 20.00 16.00 10.00 5.00 2.50
累计筛余(%) 2 24 55 95 99 100
3.4粉煤灰:粉煤灰具有以下基本效应:形态效应,活性效应的微集料效应，粉煤灰混凝土与等强度的普通混凝土相比,其性能在拌制、施工、硬化过程中都发生了很大变化。这种变化提高了混凝土的工作性即流动性、粘聚性、保水性，降低了混凝土硬化阶段的水化热，提高了混凝土强度，也提高了混凝土的抗渗性、抗侵蚀性、耐磨性等耐久性能。由于粉煤灰对混凝土的各项性能影响大，因此，其参量及本身质量一定要严格控制。本工程C65混凝土选用的是厦门嵩屿火电厂生产的I及粉煤灰，该粉煤灰细度(45um)筛余9.5%,需水量比:92%,烧失量3.72%,含水量0.5%三氧化硫含量:1.98%。其各项技术指标符合配制高性能混凝土要求。
3.5外加剂：高性能混凝土所用外加剂要满足在低水灰比条件下提高混凝土流动性的要求，所以外加剂的性能质量至关重要。为此，本工程C65高性能混凝土选用了质量可靠，性能稳定的萘系FDN高效缓凝减水剂，其各项技术指标为：密度:1.168g/ml,含固量:32.74%,PH值:6.4,砂浆减水率:19.1%，技术指标符合要求。
4.C65高性能混凝土配合比
本工程C65高性能混凝土配合比經实验室试配完成后，高性能混凝土试块经试压其28天强度均达到设计要求，配合比满足现场施工要求。C65高性能混凝土配合比结果见表4
表4 C65混凝土试验配合比:
混凝土配合比 水灰比
砂率
(%) 水泥
(kg) 水
(kg) 砂
(kg) 石
(kg) 掺合料(kg) 外加剂
(kg)
混凝土试验配合比 0.28 38 449 145 639 1039 135 16.4
5.C65高性能混凝土生产质量控制
5.1.1原材料的储存和标识
高性能混凝土专用原材料必须分厂家、品种、规格、等级存放，由于原材料的特殊重要性，须将其堆放点与其它原材料隔离，不得混仓，并作好标识，进料必须保证原材料的相对稳定。
5.1.2高性能混凝土生产前原材料的检查
高性能混凝土生产前应将生产备料做一次适应性试验，检查生产用料与其试配用原材料有无不同，如有明显差别，须从新备料。
5.1.3高性能混凝土的计量、搅拌与运输
计量混凝土原材料用的仪器、仪表，计量原材料前必须进行校准，计量精度：水泥、粉煤灰、外加剂小于+1%，砂石小于+2%，须充分保证原材料计量精度及混凝土配合比正确无误。高性能混凝土的运输要实行专车专用，在运输中混凝土运输车滚筒必须慢速正转，以避免高性能混凝土发生离析。施工中不得随意向混凝土中加水，搅拌车卸料前滚筒须先快速转动一分钟，使混凝土搅拌均匀后再卸料入泵。
6.高性能混凝土施工质量控制
高性能混凝土在施工中其可泵性不如普通混凝土，为防止混凝土堵管，保证高性能混凝土的连续施工，高性能混凝土的坍落度宜控制在200+20mm范围内。高性能混凝土在施工过程中其前期强度增长较快，若混凝土养护工作滞后或不及时高性能混凝土易产生裂缝，影响工程质量。施工中为确保高性能混凝土养护质量，可在构件较难养护的侧面紧贴挂湿润的麻袋进行覆盖养护，混凝土拆模后应及时涂刷养护剂,保证高性能混凝土得到充分养护。
7.结论
本工程 柱、墙C65混凝土浇筑完成后,按规定对C65高性能混凝土进行了现场见证试块取样，试块经广东省深圳市建筑材料检测中心试压检测,其28天抗压强度值均达到设计强度。C65高性能混凝土施工质量达到了设计、规范要求。