Ni-based superalloy K465 is brazed with BNi-2 filler metal by vacuum electron beam brazing (VEBB). In process of VEBB, effects of processing primary parameters
【机 构】
：
State Key Laboratory of Advanced Welding Production Technology,Quality Control Department
论文部分内容阅读
Ni-based superalloy K465 is brazed with BNi-2 filler metal by vacuum electron beam brazing (VEBB). In process of VEBB, effects of processing primary parameters on shear strength of joints are investigated. Microstructure of the brazed joint with BNi-2 filler metal is studied by means of scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results show that the structure of brazed seam consists of a large amount of Ni-based γ solid solution, Ni3Al (γ′), Ni3B, WB, CrB, and a small quantity of WC, NbC. The maximum shear strength of the joint is 398 MPa when the beam current of welding is 2.6 mA, heating time is 480 s and focused current is 1 800 mA.
其他文献
Hybrid polymers, poly(vinyl pyrrolidone-co-isobutyl styryl polyhedral oligomeric silsesquioxanes)s (PVP-POSS) were synthesized by one step polymerization and ch
One trial was conducted to study nutrition digestibility of Euchsaena mexicana Schrad (EMC) diets for Wulong Goose.Thirty-two geese of 9 months old were selecte
本试验的主要目的是根据不同添加比例的复合酸化剂和乳清粉对23日龄断奶仔猪生产性能的影响,从而确定复合酸化剂代替乳清粉的可行性及其合理的代替量.试验结果表明:随着复合
对4种不同退化程度的高寒草甸(未退化草甸、轻度退化草甸、中度退化草甸、重度退化草甸)土壤种子库种子用不同大小孔径分析筛进行分离处理.结果表明:未退化高寒草句可萌发种
Two new compounds involving a thiophene moiety named as 2,5-bis[4-(N,N- diphenylamino)styryl]thiophene (BPST) and 2,5-bis[4-(N,N-diethylamino)styryl]thiophene (
Background Recently, arsenic trioxide (As2O3) was considered as a novel anti-tumor agent. However, it showed severe toxicity effect on normal tissue at the same
在冀西北半干旱高寒区的两种不同类型的土壤中,进行饲用玉米产量和水分利用率的研究.结果表明:滩地玉米的产量明显高于沙地玉米.在降水一定的年份,同样的栽培条件下,滩地的储
The design and analysis of an intelligent vehicle suspension with MR dampers should address hybrid semi-active control goals, such as rejection of current-switc
An analytical expression is presented for the susceptibility of liquid cast iron to solidify according tothe Fe-C-X metastable system (also known as the chillin
A novel thermoelectric generating and performance measuring system (TGPMS) was designed and fabricated. TGPMS can not only achieve the function of thermoelectri