【摘 要】
：
对7075-T6铝合金激光复合焊焊接接头的疲劳寿命进行了探究。结果表明:疲劳裂纹萌生寿命与疲劳寿命之间存在着一定的比例关系。对于母材试样,该比值为64.5%;而对于焊接接头试
【机 构】
：
北京科技大学新金属材料国家重点实验室,西南交通大学牵引动力国家重点实验室,
论文部分内容阅读
对7075-T6铝合金激光复合焊焊接接头的疲劳寿命进行了探究。结果表明:疲劳裂纹萌生寿命与疲劳寿命之间存在着一定的比例关系。对于母材试样,该比值为64.5%;而对于焊接接头试样,该比值为20.2%。疲劳断口表面观察发现,母材试样的疲劳断口上存在大量韧窝,而焊接接头试样疲劳断口上存在许多气孔。这些气孔被认为是引起焊接接头疲劳裂纹萌生寿命急剧下降的主要原因。
The fatigue life of 7075-T6 aluminum alloy laser welded joints was investigated. The results show that there is a certain proportional relationship between fatigue crack initiation life and fatigue life. This ratio is 64.5% for the base metal sample and 20.2% for the welded joint sample. Fatigue fracture surface observation found that there are a large number of dimples on the fatigue fracture of the base metal specimen, while there are many pores on the fatigue fracture surface of the welded joint specimen. These pores are considered to be the main cause of the sharp decline in fatigue crack initiation life of welded joints.
其他文献
目的 研究早期肺癌患者呼出气特征性挥发性有机化合物(volatile organic compounds,VOCs)及其诊断价值.方法 应用固相微萃取联合气相色谱质谱技术分析117例早期肺癌患者[男54
目的 初步探讨三尖瓣人工腱索移植术治疗三尖瓣脱垂伴重度关闭不全的安全性和可靠性,并总结其应用经验.方法 回顾性分析2006年10月至2019年8月在上海交通大学医学院附属新华
机型爱立信（ERICSSON）EH237三星（SAMSUNG）SH.310三星（SAMSUNG）SH-400英福门＊＊A）INFA9000索尼（SON）C-888美国电话电报（AT＆）3630Tco（PANDA）P8500酉门子（SIEMENS）SI摩托罗拉（MOTOROLA）8900X寓士通（FUJ
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
目的 探讨迷宫Ⅳ(Maze Ⅳ)术治疗心脏瓣膜病合并持续性心房颤动(房颤)老年患者的临床效果.方法 回顾性分析2017～ 2018年我院心脏外科因心脏瓣膜病合并持续性房颤老年患者78例
闽南初夏,花果飘香。2001年6月2日上午,漳州市展览中心花团锦簇,气氛热烈,由福建省政协文教卫体委员会、福建省青年联合会、漳州市政协主办,漳州市委宣传部、诏安县委县政府
目的 系统评价远程医疗对华法林治疗管理的影响.方法 计算机检索PubMed、EMbase、Cochrane Library、 Web of Science、中国知网(CNKI)、维普中文期刊数据库(VIP)及万方数据
静脉-静脉体外膜肺氧合(VV-ECMO)作为一种体外生命支持技术已经证明其在重症呼吸衰竭患者治疗中的作用,其主要优点在于能够维持足够的氧合和清除多余的CO2,提高氧输送、改善
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
新型冠状病毒肺炎已成为世界流行性疾病,其相关抗病毒药物临床试验的结果陆续公布,阿比多尔、瑞德西韦和干扰素的疗效不明确;氯喹、羟氯喹单药治疗以及与大环内酯类药物的联