Highly coke-resisting Zr O2-decorated Ni/Al2O3 catalysts for CO methanation were prepared by a two-step process. The support was first loaded with Ni O by impregnating method and then modified with Zr O2 by deposition-precipitation method(IM-DP). Nitrogen adsorptiondesorption, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, thermogravimetric analysis, H2 temperatureprogrammed reduction and desorption, NH3temperature-programmed desorption, and zeta potential analysis were employed to characterize the samples. The results revealed that, compared with the catalysts with the same composition prepared by co-impregnation(CI) and sequential impregnation(SI) methods, the Ni/Al2O3 catalyst prepared by IM-DP showed much enhanced catalytic performance for syngas methanation under the condition of atmospheric pressure and a high weight hourly space velocity of 120000 m L g-1 h-1. In a 80 h life time test under the condition of 300–600°C and 3.0 MPa, this catalyst showed high stability and resistance to coking, and the amount of deposited carbon was only 0.4 wt%. On the contrary, the deposited carbon over the catalyst without Zr O2 reached 1.5 wt% after a 60 h life time test. The improved catalytic performance was attributed to the selective deposition of Zr O2 nanoparticles on the surface of Ni O rather than Al2O3, which could be well controlled via changing the electrostatic interaction in the DP procedure. This unique structure could enhance the dissociation of CO2 and generate surface oxygen intermediates, thus preventing carbon deposition on the Ni particles in syngas methanation. Highly coke-resisting Zr O2-decorated Ni / Al2O3 catalysts for CO methanation were prepared by a two-step process. The support was first loaded with Ni O by impregnating method and then modified with Zr O2 by deposition- precipitation method (IM-DP ). Nitrogen adsorption desorption, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, thermogravimetric analysis, H2 temperatureprogrammed reduction and desorption, NH3temperature-programmed desorption, and zeta potential analysis were employed to characterize the samples. The results revealed that, compared with the catalysts with the same composition prepared by co-impregnation (CI) and sequential impregnation (SI) methods, the Ni / Al2O3 catalyst prepared by IM-DP showed much enhanced catalytic performance for syngas methanation under the condition of atmospheric pressure and a high weight hourly space velocity of 120000 m L g-1 h-1. In a 80 h life time test under the conditions of 300-600 ° C and 3.0 MPa, this catal yst showed high stability and resistance to coking, and the amount of deposited carbon was only 0.4 wt%. On the contrary, the deposited carbon over the catalyst without Zr O2 reached 1.5 wt% after a 60 h life time test. The improved catalytic performance was attributed to the selective deposition of Zr O2 nanoparticles on the surface of Ni O rather than Al2O3, which could be well controlled via changing electrostatic contact in the DP procedure. This unique structure could enhance the dissociation of CO2 and generate surface oxygen intermediates, thus preventing carbon deposition on the Ni particles in syngas methanation.