Zonal heat treatment(ZHT) was conducted in situ to 14.5 mm-thick TC4 alloy plates by means of defocused electron beam after welding. The effects of ZHT on resid
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Zonal heat treatment(ZHT) was conducted in situ to 14.5 mm-thick TC4 alloy plates by means of defocused electron beam after welding. The effects of ZHT on residual stresses, microstructures and mechanical properties of electron beam welded joints were investigated. Experimental results show residual stresses after welding are mostly relieved through ZHT, and the maximum values of longitudinal tensile stress and transverse compressive stress reduce by 76% and 65%, respectively. The tensile strength and ductility of welded joint after ZHT at slow scanning velocity are improved because of the reduction of residual stress and the microstructural changes of the base and weld metal. ZHT at fast scanning velocity is detrimental to the ductility of welded joint, which is resulted from insufficiently coarsened alpha phase in the fusion zone and the appearance of martensite in the base metal.
其他文献
HA/316L stainless steel(316L SS) biocomposites were prepared by hot-pressing technique. The formation of bone-like apatite on the biocomposite surfaces in simul
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
The microstructures in the solidification process of aluminum twin-roll casting was simulated based on CA (Cellular Automation Method), and the nucleation model
Ca0.4Sr0.6Bi3.95Nd0.05Ti4O15 (C0.4S0.6BNT) ferroelectric thin films were prepared on Pt/Ti/SiO2/Si substrates by sol-gel method. Ef-fect of annealing process (t
A series of Eu2+-doped fluorochlorozireonate glass-ceramics were prepared by solid state reaction method. X-ray diffraction, pho-toluminescence, photo-stimulate
The Gibbs energies of liquid phases in the LaI3-MI (M=Na, K, Cs) systems were described by the modified quasi-chemical model. From the measured phase equilibriu
Ta2O5 thin films were deposited by DC reactive magnetron sputtering followed by rapid thermal annealing(RTA). Influence of sputtering pressure and annealing tem
Antimony-doped tin dioxide(ATO) nanoparticles with primary diameter in the range of 9-10 nm were rapidly synthesized via a novel combustion technique, starting
The thermoluminescence (TL) properties of Ce3+ doped NaSr4(BO3)3 phosphor under the β-ray irradiation were reported. The polycrystalline sample was synthesized
Rare earth sulfides were systematically synthesized via the sulfurization of their commercial oxide powders using CS2 gas to shorten sulfurization time, and the