The effect of swelling agent on the physicochemical properties of mesoporous hydroxyapatite particles synthesized by self-assembly process has been investigated. Cetyl trimethylammonium bromide(CTAB) and 1-dodecanethiol were used as soft template and swelling agent respectively. The results of the field emission scanning electron microscopy(FESEM), X-ray diffraction(XRD), simultaneous thermal analysis(STA), Brunauer-Emmett-Teller(BET) surface area, small-angle X-ray diffraction and Fourier transform infrared spectroscopy(FTIR)assessments revealed that in the case of low concentration, 1-dodecanethiol performed as swelling agent and caused an increase in the pore size. However, at higher concentrations it led to the formation of microemulsion and foamy structures. The optimum swelling agent: surfactant mass ratio in synthesis of mesoporous hydroxyapatite particles with high pore volume was determined to be around 2.1 in this study.
The effect of swelling agents on the physicochemical properties of mesoporous hydroxyapatite particles synthesized by self-assembly process has been investigated. Cetyl trimethylammonium bromide (CTAB) and 1-dodecanethiol were used as soft template and swelling agents respectively. The results of the field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), simultaneous thermal analysis (STA), Brunauer-Emmett- Teller (BET) surface area, small-angle X-ray diffraction and Fourier transform infrared spectroscopy (FTIR) assessments revealed that in the case of low concentration, 1-dodecanethiol performed as swelling agent and caused an increase in the pore size. However, at higher concentrations it led to the formation of microemulsion and foamy structures. The optimum swelling agent: surfactant mass ratio in synthesis of mesoporous hydroxyapatite particles with high pore volume was determined to be around 2.1 in this study.