Bituminous binders have been modified by using cocamide diethanolamide. The chemical material used in this study is used for the first-time on the purpose of modification of the bitumen. In addition to the conventional bitumen tests (penetration, softenin
【机 构】
：
Civil Engineering Department,Suleyman Demirel University,Isparta 32040,Turkey
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Bituminous binders have been modified by using cocamide diethanolamide. The chemical material used in this study is used for the first-time on the purpose of modification of the bitumen. In addition to the conventional bitumen tests (penetration, softening point and ductility tests), adhesion and peeling tests (Vialit, Nicholson and California tests) were carried out on the bituminous binders which are modified with different ratios of cocamide diethanolamide. According to the results of the tests, the most appropriate additive ratio has been determined. Samples containing the reference bituminous binder and the bituminous binder modified with the most appropriate cocamide diethanolamide ratio were prepared using the superpave volumetric mix design method (SuperpaveTM). In accordance with standard method of test for resistance of compacted asphalt mixtures to moisture-induced damage (AASHTO T 283), the moisture susceptibility of prepared samples has been examined. In order to observe the changes in strength due to the temperature difference, prepared samples were subjected to the freeze-thawing test in accordance with standard test method for resistance of concrete to rapid freezing and thawing (ASTM C 666).
其他文献
A polarizing microscope, X-ray diffraction (XRD), fourier transform infrared spectrometer (FTIR), scanning electron microscope and energy dispersive spectrometer (SEM-EDS), X-ray photoelectron spectroscopy (XPS), and micro computed tomography (Micro CT) w
Nano-pellet α-Al2O3 was prepared using aluminum nitrate as precursor and urea as fuel by a fast method of solution combustion synthesis. The formation of the nano material was dependent on the molar ratio of fuel/oxidant, calcination temperature, and fore
Aluminum sol, dry gel, and film were prepared by sol-gel and a dipping-withdrawing method. The effect of polyethylene glycol (PEG) on the behavior of aluminum sol, gel, and film was investigated by DLS, rotary viscometer, XRD, IR, EPMA, and light microsco
A quantitative pH measuring method has been used to measure the pH of pure and blended cement mortars. The blended cement mortars incorporating supplementary cementitious materials (SCMs) such as fly ash (FA), ground granulated ballast furnace slag (GGBFS
With the risk of disappearing for the rock paintings considering long-term exposure in Helan Mountain, the freeze-thaw(F-T) cycling experiments were carried out with 12-hour F-T cycling (0, 10, 20, 30, and 40 F-T cycles) under five kinds of confining pres
TiSi2 reinforced boron phenolic composites (TP) and Vitreous silica fabric reinforced TiSi2/boron phenolic composites (VTP) were prepared by compression molding, and their thermal, mechanical, ablation properties were studied. TG results show that thermal
In order to facilitate self-compacting concrete to be better used in tunnel linings that can resist fires, a SiO2 aerogel-cement mortar coating was prepared. Based on the HC curve, a self compacting concrete cube specimens coated and uncoated with SiO2 ae
To reveal and utilize the interaction between Tamm plasmon polaritons (TPPs) and two-dimensional materials are promising for exploiting next-generation optoelectronic devices. Herein, the coupling mechanism between metal TPPs and monolayer WS2 along with
Hydration-heat-inhibiting materials(HIM) with polysaccharide as core material was prepared using microcapsule sustained-releasing technology, through a centrifugal spray granulation process after melting together. The preparation process parameters of HIM
A molecular modified PCE-type GA was self-synthesized, and the grindability concerning grinding duration and particle size distribution of ground cement was evaluated. Setting time, flowability, hydration heat, mechanical properties and microstructure of