Investigation has been made into the causes of cracking in the Surfacing welding layer of Ni3Al based alloy by analysing both the liqu id-to-solid transformation in the molten pool and the distribution of thermal stress within the surfacing welding layer. The results show that cracking in the surfacing welding layer is directly related to the producing of eutectic phase β’ (NiAl) in the interdendritic region and high thermal stress within the surfacing welding layer. When the process of electric arc surfacing welding is changed from along straight line to along“ Z” pattern, cracking in the surfacing welding layer of Ni3Al based alloy is prevented due to being reduced of both the cooling rate of liquid in the molten pool and the moving speed of the heat source. Reducing the melting volume of the substrate material by lowering the output power of electric arc welding would make the content of iron atoms in the molten pool decrease. and this also can reduce the trend of the eutectic reaction in the interdendfitic region and is helpful to Suppress cracking in the surfacing welding layer.
Investigation has been made into the causes of cracking in the Surfacing welding layer of Ni3Al based alloy by analysing both the liqu id-to-solid transformation in the molten pool and the distribution of thermal stress within the surfacing welding layer. The results show that cracking in the surfacing welding layer is directly related to the producing of eutectic phase β ’(NiAl) in the interdendritic region and high thermal stress within the surfacing welding layer. When the process of electric arc surfacing welding is changed from along straight line to along “Z ” pattern, cracking in the surfacing welding layer of Ni3Al based alloy is prevented due to being reduced of both the cooling rate of liquid in the molten pool and the moving speed of the heat source. Reducing the melting volume of the substrate material by lowering the output power of electric arc welding would make the content of iron atoms in the molten pool decrease. and this also can reduce the trend of the eutectic re action in the interdenditic region and is helpful to Suppress cracking in the surfacing welding layer.