Ferroelectric materials were widely applied for actuators and sensors. Barium zirconate titanate Ba(Zr0.25Ti0.75)O3 thin film was grown on Pt/Ti/SiO2/Si(100) substrates by pulsed laser deposition. Structure and surface morphology of the thin film were studied by X-ray diffractometry(XRD) and scan electronic microscopy(SEM). The composition and chemical state near the film surface were obtained by X-ray photoelectron spectroscopy(XPS). On the sample surface,O 1s spectra can be assigned to those from the lattice and surface adsorbed oxygen ions,while C1s only result from surface contamination. The result shows that only one chemical state is found for each spectrum of Ba 3d,Zr 3d and Ti 2p photoelectron in the BZT thin film.
Ferroelectric materials were widely applied for actuators and sensors. Structure and surface morphology of the thin (Zr0.25Ti0.75) O3 thin film was grown on Pt / Ti / SiO2 / Si (100) substrates by pulsed laser deposition The composition and chemical state near the surface of the film were obtained by X-ray photoelectron spectroscopy (XPS). On the sample surface, O 1s spectra can be obtained by X-ray diffractometry (XRD) and scan electronic microscopy assigned to those from the lattice and surface adsorbed oxygen ions, while C1s only result from surface contamination. The result shows that only one chemical state is found for each spectrum of Ba 3d, Zr 3d and Ti 2p photoelectron in the BZT thin film.