【摘 要】
：
Sapphire crystals with different orientations may cone from implantation of Nb+ ions under different conditions and succedent annealing at reducing atmosphere.
【机 构】
：
Key Laboratory of Radiation Physics and Technology of Education Ministry of China,The Institute of N
论文部分内容阅读
Sapphire crystals with different orientations may cone from implantation of Nb+ ions under different conditions and succedent annealing at reducing atmosphere. Optical analysis results show that the main optical absorption bands lay in the higher energy side of the spectra in the samples. The absorption curves were evaluated by Gaussian fitting based on the F-type centers, which were confirmed by luminescence measurements. The results of Gaussian fitting show that there were F center, F+ center, F2 center, F2+ center and F2+2 center in the Nb+ ions implanted sapphire. After annealing at different temperature, all types of color centers decreased, and the higher the annealing temperature,the more the defects decreased. Sub-micrometer particles were observed by the scanning electron microscopy.
其他文献
从整个质谱学的历史来看,阵列检测器一直用来进行同时和连续的质谱测量研究.利用阵列检测器获取多道数据的好处已为人们所熟知,这包括较大的占空因素、借助比值和内标技术改
Rectification for airborne linear images is an indispensable preprocessing step. This paper presents in detail a two-step rectification algorithm. The first ste
Using 12-hydroxystearate, nonan-edioic acid and lithium hydroxide as thickener, refined mineral oil and synthetic oil as base oil, along with some structure imp
Silicon dioxide (SiO2) films were prepared on sapphire (α-Al2O3) by radio frequency magnetron reactive sputtering in order to in crease both transmission and r
Absorption of gaseous species into stationary droplets is a fundamental interest of mass transfer between liquid droplets and ambient gas, which plays a key rol
Single-phase homogeneous Ce1- xZrxO2 solid solutions with various compositions were synthesized using the reversed microemulsion method. The structural properti
Various micro-mechanical and micro-structural influences on fatigue crack growth resistance of the material have been investigated over the years. It is widely
The reduction mechanism of stainless steelmaking dust and carbon pellets was investigated. The metal oxides present in the dust were reduced by carbon with a ne
SiCf/Ti-6Al-4V composites were fabricated by the powder-coated fiber method. The precursor fiber was prepared under the optimized parameter, and the composites
Mixture of green petroleum coke, B4C and SiC together with short carbon fiber were employed as starting materials, the mixture was press-formed without any bind