Statistical analysis on probability characteristic of fatigue crack growth rate

来源 :2013年国际焊接结构疲劳断裂学术会议 | 被引量 : 0次 | 上传用户：wm3033

【摘要】

：

The standard center-cracked tensile specimens M(T)with different widths made of aluminum alloy from high-speed train were designed for fatigue crack propagation rate testing.

【作者】

：

Zhang Xiao-Chen Xie Li-Yang Liu Jian-Zhong

【机构】

：

School of Mechanical Engineering and Automation,Northeastern University,Shenyang 110819

【出处】

：

2013年国际焊接结构疲劳断裂学术会议

【发表日期】

：

2013年1期

【关键词】

：

Fatigue crack growth rate probability characteristic statistical analysis

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　The standard center-cracked tensile specimens M(T)with different widths made of aluminum alloy from high-speed train were designed for fatigue crack propagation rate testing.

其他文献

3-D fracture mechanics analyses of cracks at rib-to-deck welded joints of orthotropic steel decks

The fatigue life evaluation is very important for the safety of orthotropic steel decks.The cracks at the rib-to-deck welded joints are the defects most prone to undergo fatigue under the random loadi

会议

Phase transformationwelding residual stresses

列车车体不锈钢激光焊接工艺及接头性能分析

针对不锈钢在轨道列车上的应用，研究了SUS301L不锈钢的激光拼焊，讨论工艺参数及拼焊间隙对焊缝成形的影响，测试拼焊接头的抗晶间腐蚀性能及抗疲劳性能。

会议

列车车体SUS301L不锈钢激光拼焊腐蚀性能疲劳性能

Load history free method to predict fatigue crack growth life

A methodology is presented to predict the fatigue crack growth life under steady service load history,which can be taken as an equivalent constant amplitude load.Differing from the convention fatigue

会议

Fatiguecrack growthlife predictionstable loadhigh-speed rail

焊缝对钢制车轮弯曲应力的影响

某些型号的钢制车轮在弯曲疲劳试验中，轮辋与轮辐之间的焊缝易产生疲劳裂纹，导致车轮破坏。以往对钢制车轮进行强度分析时，多不考虑轮辋与轮辐之间的焊缝结构，将轮辋与轮辐直接处理成绑定约束，这种简化处理导致对车轮进行应力仿真计算时，难以考虑轮辋与轮辐间的过盈应力，且无法获得焊缝处的应力分布状况。

会议

钢制车轮动车组焊缝疲劳寿命

轮对服役因素对高速列车振动性能的影响

轮对型面磨耗严重影响高速列车服役振动性能，型面曲线的微小改变会引起轮轨接触性能的大幅下降，若同时考虑轮对柔性对振动的传递作用，相比轮对刚性时，构架及车体的振动加速度会发生较大变化，本文从轮对型面磨耗及其柔性入手考虑轮对服役因素对高速列车振动性能的影响。

会议

高速列车服役性能轮对磨耗轮对柔性振动加速度频谱分析

Mechanical properties of pinless friction stir welding of 2024 aluminum alloy

Joining the thin sheet aluminum alloys(<2.0 mm)are difficult via conventional friction stir welding owing to the root flaw and keyhole.In the present research,a newly designed pinless tool with involu

会议

Pinless FSW2024 aluminium alloysmechanical properties

Prediction of SCC in the heat affected zone in core shroud of boiling water reactor

Stress corrosion cracking(SCC)in the welded joint of a core shroud is the primary damage due to weld residual stress,corrosion and neutron irradiation environment in a boiling water reactor.The predic

会议

Core shroud316L stainless steelweld residual stressnumerical simulationSCC p

平行等长度表面裂纹应力强度因子复合原则

大型化工容器中存在大量的焊缝，在焊接残余应力及腐蚀介质的联合作用下，易产生垂直于焊缝的应力腐蚀裂纹，这些裂纹相互平行，且排列密集，裂纹尖端应力之间可能出现相互干涉问题，因而有必要对该类裂纹的应力强度因子复合问题进行研究，本文采用断裂力学的方法考虑平行裂纹间的相互影响，以确定合适的裂纹复合模型。

会议

应力强度因子复合裂纹平行裂纹断裂力学

Microstructure and fatigue performance of electron beam welded joints of AZ31B magnesium ahoy

10 mm thick AZ31B magnesium alloy plate was welded by the electron beam welding(EBW).The microstructure,elements distribution,tensile mechanical properties and fatigue behavior of EBW joint were measu

会议

Electron beam weldingAZ31B magnesium alloyfatigue fracturecrack propagationm

The thermodynamic behavior of AZ31B magnesium alloy under tensile and cyclic loading

Temperature evolution of AZ31B magnesium alloy plate was measured under static and cyclic loading by the approach of infrared thermograph.The mechanism of heat generation under different load level wa

会议

AZ31B alloyinfrared thermographmechanism of heat generation

Statistical analysis on probability characteristic of fatigue crack growth rate

与本文相关的学术论文