5. Corrosion Behavior of Metallic Material With Molten Nitrate Salt

Corrosion Behavior of Metallic Material With Molten Nitrate Salt

来源 :国际腐蚀工程大会(ICEC2016) | 被引量 : 0次 | 上传用户：cyfzyzclwhzy

【摘 要】

：

In a static environment,based on the heat erosion test by immersing in molten salt and electrochemical test of the heat erosion of the molten salt,the corrosion properties of the 316L,321H,P91,12CrMoV

【作 者】

：

ZHAI Wei YANG Bo ZHANG Shuanghong LI Maodong XIN Mingliang HUANG Guojia LI Shiping WANG Zhigang 

【机 构】

：

Guangzhou Special Pressure Equipment Inspection and Research Institute,510100,Research Road No.9,Hua

【出 处】

：

国际腐蚀工程大会(ICEC2016)

【发表日期】

：

2016年10期

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　In a static environment,based on the heat erosion test by immersing in molten salt and electrochemical test of the heat erosion of the molten salt,the corrosion properties of the 316L,321H,P91,12CrMoVG metal materials in the Solar Two,Hitec molten salt at different temperatures have been investigated.

其他文献

Sulfate-reducing bacteria induced the localized corrosion of Q235 steel

Localized corrosion behavior of Q235 steel in seawater containing sulphate-reducing bacteria(SRB)is investigated by wire beam electrode(WBE)technique,electrochemical measurement method and surface ana

会议

SRB induced accelerated corrosion attack of high strength steel under-0.85 VSCE cathodic polarizatio

Certain species of sulfate-reducing bacteria(SRB)use cathodes as electron donors for metabolism,and this electron transfer process may influence the proper protection potential choice for structures.

会议

The Novel Environment-friendly Chemical Conversion Nano Film

Surface and interfacial chemistry plays a critical role in developing advanced anti-corrosion systems,and the key to the successful coating system is the initial formation of a chemical conversion fil

会议

Failure analysis of pitted copper pipes used in underground water and preventive measures

The microbiologically influenced corrosion was investigated in the early failed copper pipes by pitting used in underground water.The bacteria were cultured by sampling from corrosion product near pit

会议

Erosion-corrosion of stainless steel at different locations of a 90-degree elbow

In this work,the passivation behavior and galvanic corrosion of 304 stainless steel elbow under erosion-corrosion(E-C)condition were studied by array electrodes technique through a loop system.

会议

Study on NH4Cl under deposit corrosion behavior of carbon steel

The corrosion behavior and mechanism of under deposit corrosion of ammonium chloride salt of 10# carbon steel under various temperatures and relative humidity were investigated by the weight loss meth

会议

Atmospheric Corrosion Behavior of Tin under Alternating Current Electric Field

With wide application of electronic products,they are becoming an indispensable part of our life.The service life of electronic components is attracting more and more attention.

会议

Stress Corrosion Cracking-A Common but Unfamiliar Type of Equipment Failure in Chemical Industry

Stress corrosion cracking(SCC)is a common type of equipment failure in chemical industry,especially for stainless steels equipment.However,many end users are not familiar with this failure mode when i

会议

Classifications of Different Biocorrosion Types with Practical Applications in Corrosion Analysis

Biocorrosion,also known as microbiologically influenced corrosion(MIC),is a major problem in the oil and gas industry as well as many other industrial sectors.

会议

Investigations on the Failure of an Air Preheater in a Power Plant

The failure of an air preheater is investigated in this paper.Deposit samples and corroded heating elements were taken from the air preheater of a 300MW coal-fired power plant in Wuhan Province,China,

会议