【摘 要】
：
镍钴锰三元正极材料因其高容量和较稳定的性能得到研究者的广泛关注.三元复合型材料LiNi1-x-yMnxCoyO2结合了钴酸锂、镍酸锂、锰酸锂三种材料的优点,使其具有镍酸锂的高容量特征,拥有锰酸锂低廉的价格,保持材料稳定性的优点,具备了钴酸锂稳定的结构,抑制了阳离子混排效应,使层状结构稳定的优点[1].
【机 构】
：
哈尔滨工业大学化工学院,黑龙江,哈尔滨,150001 西安汇杰实业有限公司,陕西,西安,71011
论文部分内容阅读
镍钴锰三元正极材料因其高容量和较稳定的性能得到研究者的广泛关注.三元复合型材料LiNi1-x-yMnxCoyO2结合了钴酸锂、镍酸锂、锰酸锂三种材料的优点,使其具有镍酸锂的高容量特征,拥有锰酸锂低廉的价格,保持材料稳定性的优点,具备了钴酸锂稳定的结构,抑制了阳离子混排效应,使层状结构稳定的优点[1].
其他文献
Microflower structural δ-MnO2 assembled by ultrathin nanosheets grown on three dimentional graphene nanosheets is synthesized for the first time.Herein,high conductive graphene networks (Figure 1a) ma
采用草酸沉淀法制备了一系列不同镍掺杂量的锂离子电池正极材料LiNi0.5-xMn1.5+xO4(0≤x≤0.45),研究了Ni/Mn比对于材料结构及性能的影响.X射线衍射(图1)结果显示:在x为0到0.45的范围内,所有样品都呈现尖晶石结构,随着Ni/Mn比的减小,衍射峰向高角度发生了轻微的移动,晶胞参数从x=0时的8.166(A)逐步增大到x=0.45时的8.214(A)(表1),说明镍的减少可
目前,可移动电子设备及电动汽车对电池提出更高的要求,需要电池往高能量密度发展,不同类型的高电压、高容量正极材料得到了广泛的研究.在诸多正极材料中,尖晶石型的LiNi0.5Mn1.5O4以其高电位(4.7Vvs Li/Li+),良好的可逆容量(大约135mAh/g)等优异的性能[1]表现得到了广大的关注.
LiNi0.5Mn1.5O4 (LNMO) material,with a theoretical capacity of 147 mAh g-1 and a high discharge voltage (4.7 V vs.Li/Li+) plateau,has emerged as a promising cathode material for high energy density lit
通过液相沉淀法结合高温固相法制备了Sm掺杂的LiFePO4/C,测试结果表明少量Sm掺杂能够优化颗粒形貌,减小极化过电势和传荷电阻,从而提高了材料的电化学性能.大量的Sm掺杂会形成过多的SmPO4能够阻碍材料的电化学性能.电化学测试结果表明LiFe0.99Sm0.01PO4/C在1C,2C,5C和10C下的放电容量分别为148.1,133.4,117.5和106.6mAh g-1.并且材料具有很好
LiMn1-xTixO2 (x =0,0.01,0.02,0.03) cathode materials were successfully prepared by the hydrothermal treatment of Mn2O3 and TiO2 with excess LiOH·H2O aqueous solution at 150℃.The crystal structure and
As a promising cathode materials,LiFePO4 [1] received much attentions owing to its low cost,environmental compatibility,reasonable theoretical specific capacity (ca.170 mAhg-1),acceptable operating vo
The thermal stability of a FeF3 cathode was studied by differential scanning calorimetry (DSC).The lithiated electrode was found to be more thermally stable than delithiated one.On the other hand,the
Since commercialization in 1990,the rechargeable lithium-ion batteries (LIBs) are widely used as power sources for mobile telephones,computers,toys and so on.However,extending electrode materials for
Among the existing cathode materials,V2O5 is a promising cathode candidate because of its high energy density,abundance,easy synthesis,as well as low cost.However,due to quite low diffusion coefficien