【摘 要】
:
In this paper, Pt nanowires were prepared by the alternating current deposition method using porous anodic alumina as templates.The organization morphology, crystal structure and chemical state of Pt
【机 构】
:
Faculty of science, Kunming University of Science and Technology
【出 处】
:
2014中国溶胶-凝胶学术研讨会暨国际论坛
论文部分内容阅读
In this paper, Pt nanowires were prepared by the alternating current deposition method using porous anodic alumina as templates.The organization morphology, crystal structure and chemical state of Pt nanowires were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), respectively.The electro-catalytic performance of Pt nanowires was further analyzed by cyclic voltammetry (CV) and timing current (i-t) method in potassium hydroxide solution.The results show that the diameter of Pt nanowires is about 65-75 nm, radial surfaces of nanowires present burr state.Pt nanowires are polycrystalline structure and simple substance.Pt nanowire electrode has higher electro-catalytic oxidation activity for methanol in alkaline medium than in acid medium and is about 1.38 times higher than the standard Pt/C catalyst (JM company).Moreover, the catalytic mechanism is briefly analyzed.
其他文献
The WO3 nanostructure materials have been synthesized from tungsten powder and tungsten oxide sols as precursors via sol-gel method and hydrothermal process.The structure of WO3 nanoproduct is charact
Cu species (Cu Nps, Cu2+) and Sr2+ doped Na2O-B2O3-SiO2 (NBS) glass was prepared by sol-gel and atmosphere control methods.The formation mechanism and the microstructure of the specimens were investig
We demonstrate carbon dots with tunable photoluminescence embeded in sodium borosilicate monolithic gel by sol-gel method and produce white light when directly combined with commercially available blu
A complete transparent red sodium borosilicate glass doped with Ca and Cu was synthesized by sol-gel atmosphere control method.The microstructure, size distribution and elemental composition of the na
Au quantum dots doped Na2O-B2O3-SiO2 (NBS) glass has been synthesized by both sol-gel and atmosphere control methods.The microstructure and composition of Au quantum dots in the glass was characterize
本文采用二步水热合成法,第一步在四甲基氢氧化铵水溶液中纯金属钛片上生长TiO2 6h,第二步在同样浓度的四甲基氢氧化铵水溶液中掺入极稀NaCl、LiCl、KCl在同样温度和其余条件下继续制备TiO2纳米电极6h,对其进行退火处理,并通过化学水浴沉积法(CBD)在TiO2纳米电极上沉积CdSe.然后对纳米电极形貌进行表征,并对电化学阻抗谱、光电流、电流-电压曲线的测试结果进行分析.
ZnO/polyaniline (PANI) composites were synthesized by a facile and one-pot procedure using zinc salts and aniline monomers as raw materials with aqueous chemical method.The chemical bonding establishe
论文报道了一种构筑纳米多孔二氧化钛材料的新颖方法。采用该方法,我们用钛氧笼Ti2O(OAc)2(HOAc)2Cl4制备了介孔TiO2/C复合材料A以及分级孔TiO2/C复合材料B,并对这两种新材料的电化学性能进行了研究。复合材料A具有电致变色性质,复合材料B可作为电极材料应用在超级电容器中。
利用溶胶-凝胶法及浸提技术,进行二氧化钛的固定化负载.通过XRD和SEM对其物相和微观形貌进行分析;利用甲基橙为目标污染物,探究制备以及催化工艺对二氧化钛催化降解性能的影响及其重复使用效果.结果表明:随着浸涂次数的增加,不锈钢丝网表面二氧化钛薄膜的微观形貌有所变化,对甲基橙的光催化降解效率呈现先增大后减少的趋势.浸提七次所制备的二氧化钛光催化降解效率最高,搅拌条件下的四小时紫外光降解率可达77.6
Meta-cholesterol-gelator which can self-assemble into organic nanostructure is successfully designed and synthesized, and its structure is confirmed by 1H-NMR and Mass spectra (MS).Then the Meta-chole