【摘 要】
：
With the experiment and finite element simulation, the influences of power ultrasonic on the solidification structure of 7050 aluminum alloy ingot in semi-conti
【机 构】
：
Key Laboratory of Modern Complex Equipment Design and Extreme Manufacturing,School of Mechanical and
论文部分内容阅读
With the experiment and finite element simulation, the influences of power ultrasonic on the solidification structure of 7050 aluminum alloy ingot in semi-continuous casting were researched, and the effects of casting speed on solidification structure in ultrasonic field were also analyzed. The experiment and simulation results show that the solidification structure of the ingot is homogeneously distributed, and its grain size is obviously refined at ultrasonic power of 240 W. The average grain sizes, which can be seen from the Leica microscope, are less than 100 μm. When the casting speed is 45-50 mm/min, the best grain refinement is obtained.
其他文献
Twelve samples with periodic array square pillars microstructure were prepared on the silicon wafer by plasma etching techniques, on which space b of the square
This paper is concerned with the diffusive Nicholsons blowflies equation with nonlocal delay incorporated as an integral convolution over the entire past time u
Perovskite-type oxygen-permeable membrane reactors of BaCo0.7Fe0.2Nb0.1O 3 -δ (BCFNO) packed with Ru-based catalyst had high oxygen permeability and could be u
The hot-compression of Al-1Mn-1Mg (mass fraction, %) alloy sample was carried out on a Gleeble-1500 thermo-simulator at deformation temperatures from 320 to 400
CdZnTe wafers were machined by lapping and mechanical polishing processes, and their surface and subsurface damages were investigated.The surface damages are ma
住宅消费的满足程度不仅取决于自身的居住空间,还受到邻居行为、社区公共环境等影响。分析了住宅消费外部性产生的原因和影响,提出了治理住宅消费外部性的相关对策。
Satisf
The electromechanical properties of metallic single-walled carbon nanotubes (SWCNTs) in the electric field are demonstrated with a column shell model in this pa
The bulk metallic glassy (BMG) rods of [(Fe0.5Co0.5)0.72B0.192Si0.048Nb0.04]100-xYx (x=0-6) and [(FexCo1-x)0.72B0.192Si0.04]Nb0.04]96Y4 (x=0.5-0.8) were prepare
The factors involved in simulating the continuous casting process of steel and the effects of the factors on the thermal behavior were investigated. The numeric
Nanocrystalline single-phase alloys with the nominal compositions (at%) of Nd12.3-xDyxFe79.7Zr0.8Nb0.8Cu0.4B60 (x=0, 0.5,1.5, and 2.5) were prepared by melt-sp