Top seeded infiltration and growth technique (TSIG) is an effective method for the preparation of high quality large YBa2Cu3O7-x (YBCO) bulk superconductors. In this paper, single domain YBCO bulk superconductors, with different Y2Ba4CuWOy (YW2411) additions, have been fabricated by TSIG process. the solid phase pellet is made of a mixture of Y2BaCuO5(Y211) + xwt% YW2411 powders, x=0, 1, 3, 5, 7, 9. The growth morphology, microstructure and levitation force of the YBCO bulks have been investigated, it is found that the levitation force is increasing from 23.05 to 33.6 N with the increasing of YW2411 addition from 0 to 5wt%, and decreasing from 33.6 to 21.59 N with the increasing of YW2411 addition from 5 to 9wt%,the largest levitation force is obtained when the YW2411 content is about 5wt%. This is very important for us to fabricate high quality YBCO bulk superconductors.
In this paper, single domain YBCO bulk superconductors, with different Y2Ba4CuWOy (YW2411) additions, have been fabricated (TSB) is an effective method for the preparation of high quality large YBa2Cu3O7-x (YBCO) bulk superconductors. by TSIG process. The solid phase pellet is made of a mixture of Y2BaCuO5 (Y211) + xwt% YW2411 powders, x = 0,1,3,5,7, 9. The growth morphology, microstructure and levitation force of the YBCO bulks has been investigated, it is found that the levitation force is increased from 23.05 to 33.6 N with the increasing of YW2411 addition from 0 to 5 wt%, and decreasing from 33.6 to 21.59 N with the increasing of YW2411 addition from 5 to 9 wt%, the largest levitation force is obtained when the YW2411 content is about 5 wt%. This is very important for us to fabricate high quality YBCO bulk superconductors.