AF 导线冷剥线工艺的检验结果为我们揭示了一个严重的质量隐患。按照正常的冷剥线工艺送行操作,竞有高达80%以上的导线铜丝受到不同程度的损伤,严重的甚至断丝。这种情况在高可靠的航天产品中是不能允许的。上述结果表明,这个质量隐患不是由于工人师傅操作不慎或技术不精所造成的,而是冷剥线工艺本身的缺陷所引起的后果。类似这样的问题,在其它生产部门、甚至科研单位还有没有?应引起有关领导和管理部门的重视。
The test results of the AF wire cold stripping process revealed a serious quality risk for us. In accordance with the normal cold stripping process delivery operation, competing up to 80% of the wire copper wire by different degrees of damage, serious or even broken wire. This situation is not allowed in highly reliable aerospace products. The above results show that this quality is not due to hidden dangers caused by improper operation of workers or technically poor, but the cold stripping process itself caused by defects in the consequences. Similar to this question, in other production departments, even scientific research units still? Should draw the attention of the leadership and management departments.