In this paper, the microstructure and mechanical properties of Al-Si-Cu-Mg casting alloy under different solution conditions were investigated by optical metallographic and mechanical property test. The results show that the cast alloys were composed of α-Al, primary Si, eutectic Si, Al2Cu and Al7Cu2Fe phases. Three changes took place during solution treatment: Firstly, with the increase of solution temperature and the solution holding time extension, more and more Al2Cu phase was dissolved into the matrix; Secondly, with the increase of solution temperature and the solution holding time extension, morphology of eutectic Si, Al7Cu2Fe and other insoluble phases changed into more round; Thirdly, at the fixed solution temperature, if the solution time extended too long, it would cause grains, eutectic Si and other insoluble phases aggregated and coarsened. About mechanical properties, when the solution time was fixed, the hardness, tensile strength and the yield strength of the Al-Si-Cu-Mg alloy treated by T6 enhanced while the solution temperature increasing, and when the solution temperature was fixed, the ultimate tensile strength and the elongation of the Al-Si-Cu-Mg alloy treated by T6 increased at first and then decreased while the solution time increasing, but the hardness of the alloys affected less by the solution time. In this paper, the microstructure and mechanical properties of Al-Si-Cu-Mg casting alloy under different solution conditions were investigated by optical metallographic and mechanical property test. The results show that the cast alloys were composed of α-Al, primary Si, Three changes took place during solution treatment: Firstly, with the increase of solution temperature and the solution holding time extension, more and more of Al2Cu phase was dissolved into the matrix; Secondly, with the increase of solution temperature Thirdly, at the fixed solution temperature, if the solution time extended too long, it would cause grains, eutectic Si and other insoluble phases aggregated and coarsened. About mechanical properties, when the solution time was fixed, the hardness, tensile strength and the yield strength of the Al-Si-Cu- Mg alloy treated by T6 enhanced while the solution temperature increased, and when the solution temperature was fixed, the ultimate tensile strength and the elongation of the Al-Si-Cu-Mg alloy treated by T6 increased at first and then decreased while the solution time increasing, but the hardness of the alloys affected less by the solution time.