Chitosan-hydroxyapatite (CS-HA) composite powders were synthesized via in situ co-precipitation method, through the reaction of Ca(NO3)2 and H3PO4 in the simula
【机 构】
：
School of Chemical Engineering and Materials
论文部分内容阅读
Chitosan-hydroxyapatite (CS-HA) composite powders were synthesized via in situ co-precipitation method, through the reaction of Ca(NO3)2 and H3PO4 in the simulated body fluid (SBF) containing appropriate amount of chitosan. The thermal evolution, microstructure and morphology were studied by TG-DTA (thermogravimetry-differential thermal analysis), XRD (X-ray diffraction), FTIR (Fourier transform infrared spectroscopy) and TEM (transmission electron microscopy). The in vitro bioactivity test showed that the obtained CS-HA composites had higher capability of inducing calcium ions deposition. Effects of CS-HA composites on the bioactivity and compressive strength of bioglass bone cement were investigated. The results indicated that the bioactivity of bioglass bone cement could be improved further when CS-HA composite powders were added into the cement, and appropriate amount of CS-HA additive was favorable for compressive strength improvement of bioglass bone cement.
其他文献
The electric measurements were carried out for La0.8Sr0.2CoO3 nanoceramics by using impedance spectroscopy methods. The re- sistance of sample was practically i
The flow characteristics of aluminum coated boron steel in hot press forming were investigated.Furthermore,the effects of aluminum coated layer on press forming
The structural characteristics of the trivalent chromium deposits and their interfacial behavior in the plating solution with and without polyethylene glycol mo
Electrochemical corrosion of Ti-35Nb-5Ta-7Zr alloy fabricated by arc melting and heat treatment process was studied in 0.9% NaCl at (37±1) ℃. Phase and micros
By temperature gradient method under high pressure and high temperature (HPHT), with NiMnCo alloy as the solvent metal, at diamond-stable region of about 5.4 GP
Ti-Hf binary alloys contained 10%,20%,30% and 40%(mass fraction)Hf were manufactured in the vacuum furnace system.And then,specimens were homogenized for 24 h a
TiAl3-Al coating was deposited on orthorhombic Ti2AlNb alloy substrate by cold spraying with the mixture of pure Al and Ti as the feedstock powder at a fixed mo
Polysiloxane/SiO2 hybrid coatings have been prepared on Kapton films by a sol-gel process. The erosion resistance of polysiloxane/SiO2 (20 wt pct) coating was e
The electrical properties of solder contact layers between Cu-Ni shunt metal and tube type Bi2212 superconductor that is applied in superconducting fault curren
Because of the various excellent characteristics of cast basalt materials, such as, anti-corrosion, anti-wearing, good hardness, high chemical stability, of whi