它进一步交联同化后便得到高度交联的固化体。由于其高透明性及高硬度,外观似玻璃,故该树脂有玻璃树脂之美称。它对紫外光有高度的透明性,因而是优良的耐紫外涂层。然而,这种玻璃树脂固化体质脆,作为涂层,其可涂厚度通常在20μm 以下。若将它配以高量填料,则该有色涂层极易开裂。为克服其脆性。Gilligan 等采用(CH_3)_3SiCl 作为硅基化试剂与玻璃树脂溶液在 DMF 中0℃下进行反应,成功地使三甲基硅氧基(CH_3)_3SiO 取代树脂中部分硅醇基,制得韧性硅基化玻璃树脂2作为 It is further crosslinked and assimilated to obtain a highly cross-linked cured body. Because of its high transparency and high hardness, looks like glass, so the resin has the reputation of glass resin. It is highly transparent to UV light and is therefore an excellent UV-resistant coating. However, this glass-resin cured body is brittle, and as a coating, its coatable thickness is usually below 20 μm. If it is accompanied by a high amount of filler, the colored coating is very easy to crack. To overcome its fragility. Gilligan and other (CH_3) _3SiCl as a silylating agent and the glass resin solution in DMF at 0 ° C for the reaction, the successful trimethylsiloxy (_3SiO_3SiO) to replace part of the silanol resin, the toughness of silicon Based glass resin 2 as