利用X射线定量织构分析术和背散射电子衍射花样术,研究了冷轧 LY12铝合金的再结晶 织构及重位(CSL)晶界的分布,结果表明,高温退火样品的再结晶织构与冷轧样品的织构相似;预回复 低温退火具有增强再结晶立方{001}<100>织构和降低退火S{123}<634>、C{112}<111>及 B{110}}<112>织构组分的作用;高强度的再结晶立方织构和一定强度的S织构共存的样品,∑7重 位晶界具有较高的出现频度。
X-ray quantitative texture analysis and backscattered electron diffraction patterning were used to study the recrystallization texture and the distribution of heavy-grain (CSL) grain boundaries in the cold-rolled LY12 aluminum alloy. The results show that the recrystallization texture Which is similar to that of cold-rolled samples. The pre-annealed low-temperature annealing has the advantages of enhanced recrystallization cubic {001} <100> texture and reduced annealing S {123} <634>, C {112} <111> and B {110} The effect of <112> texture components; high-intensity recrystallized cubic texture and a certain strength of S texture coexist samples, Σ7 heavy grain boundaries have a higher frequency of occurrence.