Cement raw meal with MSS and different heavy metals was blended to examine the fixation ratios, chemical species, and cement crystalline phases in clinkers. The results showed that blending MSS could decrease the fixation ratio of Cr, Ni, Cu, and Zn in th
【机 构】
：
College of Environmental Science and Engineering, State Key Laboratory of Pollution Control and Reso
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Cement raw meal with MSS and different heavy metals was blended to examine the fixation ratios, chemical species, and cement crystalline phases in clinkers. The results showed that blending MSS could decrease the fixation ratio of Cr, Ni, Cu, and Zn in the produced clinker by 5％ to 25％. And Cr, Cu, and Zn were mainly incorporated into clinkers as metal silicates, Ni was mainly solubilized in Mg O to form magnesium nickel oxides, and the transition phases were mainly metal aluminum oxides as indicated by X-ray diffraction. The reduction of fixation ratios was likely attributed to the presence of impure elements, such as sodium and phosphorus in MSS. In addition, high concentrations (eg, 1.7 wt％) of chlorine in MSS led to metal chloride formation that could vaporize Cu, Cr, Ni, and Zn. To summarize, introducing MSS would decrease the fixation ratios of heavy metals due to the presence of impure elements, such as sodium and phosphorus and chlorine.
其他文献
To study the extraction difficulty of lithium ions from various crystal planes of Li2TiO3,according to the first principle,four representative crystal surfaces of Li2TiO3(precursor),(-133),(-206),(002) and(-131),were selected to establish a model and to c
The pastes containing different dosages of fly ash were taken into ultraviolet radiation and low temperature freeze condition simultaneously(URL) for 30 days and only ultraviolet radiation condition(UR) for 30 days after standard curing,so as to investiga
Taking dodecanethiol as the representative, we investigated the corrosion inhibition perfor-mance of SAL in seawater under pressures from 0.1 to 9 MPa. By using scanning Kelvin probe, the dodeca-nethiol SAL is confirmed to build on Cu surface, and the mod
To develop an efficient and bio-compatible way to improve the thermal and mechanical properties of addition type liquid silicone rubber (LSR),a series of modified LSR samples were prepared by introducing octavinyl-polyhedral oligosilsesquioxanes (VPOSS) a
To efficiently utilize the kaolin, an economical way of preparing cordierite ceramic with high performance for electric heater supports was put forward. In this study, sintering process, phase transformation, microstructure evolutions were systematically
A new type of capric acid (CA)-acid expanded vermiculite (AEV) composite phase change material (PCM) with improved adsorption ability and interface adhesive strength was developed. Through the analysis of non-isothermal phase transition kinetics, modified
The isothermal absorption properties and kinetic model of Cr (Ⅵ) and Cr (Ⅲ) onto ettringite were investigated using the batch adsorption method. IR analysis was used to study the difference and mechanism of the adsorption of chromium ions with different v
The mechanical and thermal properties of steel reinforced concrete columns with CFRP reinforcement were examined after exposure to a high temperature of 500℃. The concrete made with normal and recycled coarse aggregate (RCA) was fabricated and three diffe
Due to the intrinsic nature of a heterogeneous and anisotropic microstructure of cement based materials and the small indentation size, the measured microhardness values are subject to considerable variability. This work presents an in-depth assessment of