Silver matrix composite brushes were fabricated by means of powder metallurgy,which included pressing at 300 MPa and then sintering for 1 h in pure H2 protective atmosphere at 700℃ and repressing at 500 MPa.Four kinds composites with different compositions were produced,and the mechanical properties and electrical wear performance were investigated.The results showed that the composite added with carbon nanotubes had a higher hardness and strength,a lower contact voltage drop and an excellent anti-wear property in electrical sliding wear,because of the reinforcement ability of carbon nanotubes.Adding graphite to the composite also decreased the wear loss and contact voltage drop,because graphite had an electrical current conducting ability which not only made the current pass the lubricating films easily but also eliminated and reduced the arc and spark effectively.
Silver matrix composite brushes were fabricated by means of powder metallurgy, which included pressing at 300 MPa and then sintering for 1 h in pure H2 atmosphere at 700 ° C and repressing at 500 MPa. Four kinds of composites with different compositions were produced, and the mechanical properties and electrical wear performance were investigated. The results showed that the composite added with carbon nanotubes had a higher hardness and strength, a lower contact voltage drop and an excellent anti-wear property in electrical sliding wear, because of the reinforcement ability of carbon nanotubes .Adding graphite to the composite also decreased the wear loss and contact voltage drop, because graphite had an electrical current conducting ability which not only made the current pass the lubricating films but also eliminated and reduced the arc and spark effectively.