从氯丁橡胶的防护体系、增塑剂和补强填充剂等方面对其耐热老化性能进行了研究.结果表明,防护体系采用防老剂ZA/NBC和微晶蜡并用,增塑剂使用TOTM/TP95,补强填充体系选择无机填料和炭黑并用可有效提升氯丁橡胶的耐热老化性能.
氯丁橡胶耐热老化性能的研究
【摘 要】
：
从氯丁橡胶的防护体系、增塑剂和补强填充剂等方面对其耐热老化性能进行了研究.结果表明,防护体系采用防老剂ZA/NBC和微晶蜡并用,增塑剂使用TOTM/TP95,补强填充体系选择无机填料和炭黑并用可有效提升氯丁橡胶的耐热老化性能.
【机 构】
：
青岛科技大学,山东青岛 266000;北汽福田汽车股份有限公司,北京昌平 102206;青岛科技大学,山东青岛 266000;青岛晟科材料有限公司,山东青岛 266000;山东美晨工业集团有限公司,山
【出 处】
：
特种橡胶制品
【发表日期】
：
2021年4期
其他文献
通过设计符合硬丁腈性能标准的软丁腈胶料配方,对比了可塑度、硫化特性以及粘合性能.结果 表明,替代后的软丁腈橡胶各项性能均能满足硬丁腈性能的指标要求,且软丁腈与硬丁腈相比具有更好的加工性能.
试验研究了1000℃4h和1060℃4h固溶处理后022Cr22Ni5Mo3N钢Φ75 mm材的组织和力学性能.结果 表明,022Cr22Ni5Mo3N钢Φ75 mm材终锻温度970℃空冷的组织(体积分数)约为铁素体31％,奥氏体56％,析出物13％;1000℃4h固溶后为铁素体38％,奥氏体60％,析出物2％;1060℃4h固溶后铁素体50％,奥氏体50％,该钢通过采用1060℃固溶后,拉伸断裂强度731 MPa,延伸率38％,冲击功AKV(-40℃)76 ～81 J,满足标准要求.
The increasing demand of the green energy storage system en-courages us to develop a higher energy storage system to take the place of the present lithium-ion batteries with limited en-ergy/power densities [1,2]. Among the diverse candidates, lithium–sulf
Ni3S2 nanorods growing directly on Ni foam for all-solid-state asymmetric supercapacitor and efficie
Transition metal compounds are attractive for their significant applications in supercapacitors and as non-noble metal catalysts for electrochemical water splitting. Herein, we develop Ni3S2 nanorods grow-ing directly on Ni foam, which act as multifunctio
The light weight, good bending resistance and low production cost make flexible perovskite solar cells (PSCs) good candidates in wearable electronics, portable charger, remote power, and flying objects. High power conversion efficiency (PCE) plays a cruci
Efficient and stable planar all-inorganic perovskite solar cells based on high-quality CsPbBr3 films
All-inorganic cesium lead bromide (CsPbBr3) perovskite is attracting growing interest as functional ma-terials in photovoltaics and other optoelectronic devices due to its superb stability. However, the fabri-cation of high-quality CsPbBr3 films still rem
Identification of reversible insertion-type lithium storage reaction of manganese oxide with long cy
Recently, MnO2 has gained attention as an electrode material because of its very high theoretical capacity and abundant availability. However, the very high volumetric change caused by its conversion-type reac-tion results in bad reversibility of charge-d
Herein, the relationship between the structure and base properties of Mg–Al hydrotalcite catalysts was comprehensively investigated in relation to heat treatment and rehydration processes, which are well known as memory effects of hydrotalcite. The struct
P(VDF-HFP)-poly(sulfur-1,3-diisopropenylbenzene) functional polymer electrolyte for lithium–sulfur b
Lithium–sulfur (Li–S) battery as a high-energy density electrochemical energy storage system has at-tracted many researchers\' attention. However, the shuttle effect of Li–S batteries and the challenges associated with lithium metal anode caused poor cy
Lithium sulfur (Li-S) batteries are the promising power sources, but their commercialization is signifi-cantly impeded by poor energy-storage functions at high sulfur loading. Here we report that such an issue can be effectively addressed by using a musse