By using a sol-gel clue,a set of polycrystalline perovskite samples La1-xAgxMnO3 with a nominal doping level ranging from 0.05 to 0.45 has been synthesized.The chemical composition and the magnetism of the samples were investigated.A little Ag was found seeping from the samples in the sintering process when the doping level exceeded 0.05 and the sintering temperature was higher than 700°C resulting in the samples being in multiphase.The magnetic transition points of the samples have been found to decrease with increasing sintering temperature.A concentrationdependent Tc similar to that of bivalent metal ion doped perovskite,has been obtained.We believe that the Ag seeping in the sintering process is responsible for those magnetic characteristics.