A series of Ba1-xSrxTi1-yZryO3 (0≤x≤0.5, 0≤y≤0.4) and Ba1-xZnxTi1-ySnyO3 (0≤x≤0.3, 0≤y≤0.3) solid solutions were synthesized by Iow-temperature/Iow-pressure hydrothermal method below 170℃, 0.8 MPa. XRD pattern and cell parameters-composition figures of these prepared powders demonstrated that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM showed that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of those powders doped by Sr2+ and Zr4+ or Zn2+ and Sn4+ have dielectric constant twelve times higher than and dielectric loss 1/6 those of pure BaTiO3 phase at room temperature.