Effect of Nanophase on the Nucleation of Intragranular Ferrite in Microalloyed Steel

来源 :Journal of Wuhan University of Technology(Materials Science | 被引量 : 0次 | 上传用户:yangchengwang0
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
MnS, MnS+V(C, N) complex precipitates in micro-alloyed ultra-fine grained steels were precisely analyzed to investigate the grain refining mechanism. The experimental results shows that MnS, MnS+V(C, N) precipitates provide nucleation center for Intra-granular ferrite (IGF), so that refined grain remarkably. Moreover, substructures such as grain boundary, sub-boundary, distortion band, dislocation and dislocation cell in austenite increased as the deformation energy led by heavy deformation at low temperature (deformation temperature≤800 ℃, deformation quantity≥50%). As a result, V(C, N) nanophase precipitated at these substructures, which pinned and stabilized substructures. The substructures rotated and transformed into ultra-fine ferrite. 20 nm-50 nm were the best grain size range of V(C, N) as it provided nucleating center for intragranular ferrite. The grain size of V(C, N) were less than 30 nm in the microalloyed steels that with volume ratio of ultra-fine ferrite more than 80% and grain size less than 4 μm. MnS, MnS + V (C, N) complex precipitates in micro-alloyed ultra-fine grained steels were precisely defined to investigate the grain refining mechanism. The experimental results shows that MnS, MnS + V for intra-granular ferrite (IGF), so that refined grain remarkably. Moreover, substructures such as grain boundary, sub-boundary, distortion band, dislocation and dislocation cell in austenite increased as the deformation energy led by heavy deformation at low temperature deformation≤50%). As a result, V (C, N) nanophase precipitated at these substructures, which pinned and stabilized substructures. The substructures rotated and transformed into ultra-fine ferrites. 20 nm-50 nm were the best grain size range of V (C, N) as it provided nucleating center for intragranular ferrite. The grain size of V (C, N) were less than 30 nm in the microalloyed steels that with volume ratio of ultra-fine ferrite more than 80% and grain size less than 4 μm.
其他文献
在使用新教材的过程中,我们注意到了低年级图文结合的应用题,是新教材的一大亮点,这类应用题的编写充分考虑了低年级学生的年龄特点,充满了童趣,贴近学生生活。在教学过程中,
期刊