摘要：分析了混凝土裂缝产生的原因，为了保证现浇混凝土效果和耐久性，除了正确合理的设计以外，必须严格提高施工技术水平，裂缝的出现不但会影响结构的整体性和刚度，还会引起钢筋的镑蚀、加速混凝土的碳化、降低混凝土的耐久性和抗疲劳、抗渗能力。因此根据裂缝的性质和具体情况我们要区别对待、及时处理，以保证建筑物的安全使用。
关键词：混凝土;现浇;裂缝;质量;控制措施
Abstract: the author analyzes the cause of concrete crack, in order to guarantee cast-in-situ concrete effect and durability, besides right outside the reasonable design, must be strictly improve the construction technology level, the occurrence of crack will not only affect the structure of integrity and stiffness, can also cause corrosion of reinforcement concrete, accelerating the pound carbide, reduce the durability of concrete and resist fatigue, anti-permeability ability. Therefore according to the nature of the cracks and circumstances we should be kept separate, handled in a timely manner, to ensure the safe use of the building.
Keywords: concrete; The site; Crack; Quality; Control measures
中图分类号： TU528 文献标识码：A 文章编号：
混凝土施工过程中，裂缝的产生不可能完全避免，只要裂缝的数量、形状及发展趋势不会影响建筑物的受力及表面感观，就可以不进行处理。如果裂缝的发展有可能对建筑物的整体受力造成严重影响，或建筑物表面裂缝影响了人们的感观舒适度，给人造成危险感，那就有必要对裂缝进行控制和治理。目前，不同规范对建筑物所要求的耐久性、美观度不同，对需要处理的裂缝规定也有所不同。以下从几方面对混凝土裂缝产生的原因和防治措施进行论述，供技术人员参考。
1、大体积混凝土产生裂缝的主要原因
1.1水泥水化热
水泥在水化过程中要释放出一定的热量，而大体积混凝土结构断面较厚，表面系数相对较小，所以水泥发生的热量聚集在结构内部不易散失。这样混凝土内部的水化热无法及时散发出去，以至于越积越高，使内外温差增大。单位时间混凝土释放的水泥水化热，与混凝土单位体积中水泥用量和水泥品种有关，并随混凝土的龄期而增长。由于混凝土结构表面可以自然散热，实际上内部的最高温度，多数发生在浇筑后的最初3～5天。
1.2外界气温变化
大体积混凝土在施工阶段，它的浇筑温度随着外界气温变化而变化。特别是气温骤降，会大大增加内外层混凝土温差。应采取温度控制措施，防止混凝土内外温差引起的温度应力。
1.3混凝土的收缩
混凝土收缩的主要原因是内部水蒸发引起混凝土收缩。干湿交替会引起混凝土体积的交替变化，这对混凝土是很不利的。
2、混凝土裂缝裂缝处理措施
混凝土裂缝的修补措施主要有以下一些方法：表面修补法，灌浆、嵌逢封堵法，结构加固法。混凝土置换法，电化学防护法以及仿生自愈合法。
2.1表面修補法
表面修补法是一种简单、常见的修补方法，它主要适用于稳定和对结构承载能力没有影响的表面裂缝以及深进裂缝的处理。通常的处理措施是在裂缝的表面涂抹水泥浆、环氧胶泥或在混凝土表面涂刷油漆、沥青等防腐材料，在防护的同时为了防止混凝土受各种作用的影响继续开裂，通常可以采用在裂缝的表面粘贴玻璃纤维布等措施。
2.2灌浆、嵌逢封堵法
灌浆法主要适用于对结构整体性有影响或有防渗要求的混凝土裂缝的修补，它是利用压力设备将胶结材料压人混凝土的裂缝中，胶结材料硬化后与混凝土形成一个整体，从而起到封堵加固的目的，常用的胶结材料有水泥浆、环氧树脂、甲基丙烯酸酯、聚氨酯等化学材料。
嵌缝法是裂缝封堵中最常用的一种方法，它通常是沿裂缝凿槽，在槽中嵌填塑性或刚性止水材料，以达到封闭裂缝的目的。常用的塑性材料有聚氯乙烯胶泥、塑料油膏、丁基橡胶等等；常用的刚性止水材料为聚合物水泥砂浆。
2.3结构加固法
当裂缝影响到混凝土结构的性能时，就要考虑采取加固法对混凝土结构进行处理。结构加固中常用的主要有以下几种方法：加大混凝土结构的截面面积。在构件的角部外包型钢、采用预应力法加固、粘贴钢板加固、增设支点加固以及喷射混凝土补强加固。
2.4混凝土置换法
混凝土置换法是处理严重损坏混凝土的一种有效方法，此方法是先将损坏的混凝土剔除，然后再置换人新的混凝土或其他材料。常用的置换材料有：普通混凝土或水泥砂浆、聚合物或改性聚合物混凝土或砂浆。
2.5电化学防护法
电化学防腐是利用施加电场在介质中的电化学作用，改变混凝土或钢筋混凝土所处的环境状态。钝化钢筋，以达到防腐的目的。阴极防护法、氯盐提取法、碱性复原法是化学防护法中常用而有效的三种方法。这种方法的优点是防护方法受环境因素的影响较小，适用钢筋、混凝土的长期防腐，既可用于已裂结构也可用于新建结构。
2.6仿生自愈合法
仿生自愈合法是一种新的裂缝处理方法，它模仿生物组织对受创伤部位自动分泌某种物质，而使创伤部位得到愈合的机能，在混凝土的传统组分中加入某些特殊组分(如含粘结剂的液芯纤维或胶囊)，在混凝土内部形成智能型仿生自愈合神经网络系统，当混凝土出现裂缝时分泌出部分液芯纤维可使裂缝重新愈合。
3、大体积混凝土的配合比设计
3.1水泥的选用
应尽量选用水化热低、凝结时间长的水泥，优先采用中热硅酸盐水泥、低热矿渣硅酸盐水泥、大坝水泥、矿渣硅酸盐水泥、粉煤灰硅酸盐水泥、火山灰质硅酸盐水泥等。
3.2粗细骨料
粗骨料宜采用连续级配，细骨料宜采用中砂。大体积混凝土在保证混凝土强度及坍落度要求的前提下，应提高掺合料及骨料的含量，以降低单方混凝土的水泥用量。
3.3减水剂
为满足和易性和减缓水泥早期水化热发热量的要求，宜在混凝土中掺入适量的缓凝型减水剂。除加入减水剂外，有些混凝土还要根据需要加入其他外加剂，如引气剂、膨胀剂、泵送剂等。
3.4除以上3点外，还要适当降低原材料的温度。
4、浇筑时采取的措施
浇筑方案，除应满足每一处混凝土在初凝以前就被上一层新混凝土覆盖并捣实完毕外，还应考虑结构大小、钢筋疏密、预埋管道和地脚螺栓的留设、混凝土供应情况以及水化热等因素的影响，常用方法有以下2种：
4.1全面分层。即在第一层全面浇筑全部浇筑完毕后，再回头浇筑第二层，此时应使第一层混凝土还未初凝，如此逐层连续浇筑，直至完工为止。采用这种方案，适用于结构平面尺寸一般不宜太大，施工时从短边开始，沿长边推进比较合适。必要时可分成两段，从中间向两端或从两端向中间同时进行浇筑分段分层。混凝土浇筑时，先从底层开始，浇筑至一定距离后浇筑第二层，如此依次向前浇筑其他各层。由于总的层数较多，所以浇筑到顶后，第一层末端的混凝土还未初凝，又可以从第二段依次分层浇筑。这种方案适用于单位时间内要求供应的混凝土较少，结构物厚度不太大而面积或长度较大的工程。
4.2斜面分层。要求斜面的坡度不大于1/3，适用于结构的长度超过厚度3倍的情况。混凝土从浇筑层下端开始，逐渐上移。
5、大体积混凝土养护措施
要尽量长时间保持混凝土湿润状态，避免干缩，使混凝土能够增长强度以抵抗开裂应力。当表面可能干燥很快时，必须连续充分湿润养护以求获得好的表面强度。目前，大体积混凝土常用的养护方法是保温隔热法。采用的表面保温材料包括：保温被、不吸水的泡沫塑料板、聚苯乙烯泡沫塑料板、草袋、砂层保温及喷涂保温层等。在尽量减少混凝土内部温升的前提下，大体积混凝土的养护是一项关键的工作，必须切实做好。
保温的目的主要是为了减少混凝土表面的热扩散，减小混凝土表面的温度梯度，延长散热时间，充分发挥混凝土强度的潜力和材料松弛特性，防止产生表面裂缝。保湿养护的作用是：一是浇筑不久尚处于凝固硬化阶段的混凝土，水化的速度较快，适宜的潮湿条件可防止混凝土表面的脱水而产生收缩裂缝：二是混凝土在保温及潮湿条件下可使水泥的水化作用顺利进行，提高混凝土的抗拉强度。
6、结语
大体积混凝土产生裂缝是由多种原因造成的，在大体积混凝土施工中，合理选择施工材料，优化混凝土配合比，优化混凝土的供应，采用科学的施工方法，严格施工管理，加强大体积混凝土养护，就可以低混凝土温度应力和提高混凝土本身抗拉性能，保证工程质量。
参考文献
1牛紫龙，混凝土施工中温度裂缝的分析与控制，工程建设，2006.
2趙志缙，赵帆．高层建筑施工（第二版） 中国建筑工业出版社，2005.1
3杨启欧．论高层建筑混凝土施工技术《广东科技》。2007年第03期
注：文章内所有公式及图表请用PDF形式查看。
关键词：混凝土;现浇;裂缝;质量;控制措施
Abstract: the author analyzes the cause of concrete crack, in order to guarantee cast-in-situ concrete effect and durability, besides right outside the reasonable design, must be strictly improve the construction technology level, the occurrence of crack will not only affect the structure of integrity and stiffness, can also cause corrosion of reinforcement concrete, accelerating the pound carbide, reduce the durability of concrete and resist fatigue, anti-permeability ability. Therefore according to the nature of the cracks and circumstances we should be kept separate, handled in a timely manner, to ensure the safe use of the building.
Keywords: concrete; The site; Crack; Quality; Control measures
中图分类号： TU528 文献标识码：A 文章编号：
混凝土施工过程中，裂缝的产生不可能完全避免，只要裂缝的数量、形状及发展趋势不会影响建筑物的受力及表面感观，就可以不进行处理。如果裂缝的发展有可能对建筑物的整体受力造成严重影响，或建筑物表面裂缝影响了人们的感观舒适度，给人造成危险感，那就有必要对裂缝进行控制和治理。目前，不同规范对建筑物所要求的耐久性、美观度不同，对需要处理的裂缝规定也有所不同。以下从几方面对混凝土裂缝产生的原因和防治措施进行论述，供技术人员参考。
1、大体积混凝土产生裂缝的主要原因
1.1水泥水化热
水泥在水化过程中要释放出一定的热量，而大体积混凝土结构断面较厚，表面系数相对较小，所以水泥发生的热量聚集在结构内部不易散失。这样混凝土内部的水化热无法及时散发出去，以至于越积越高，使内外温差增大。单位时间混凝土释放的水泥水化热，与混凝土单位体积中水泥用量和水泥品种有关，并随混凝土的龄期而增长。由于混凝土结构表面可以自然散热，实际上内部的最高温度，多数发生在浇筑后的最初3～5天。
1.2外界气温变化
大体积混凝土在施工阶段，它的浇筑温度随着外界气温变化而变化。特别是气温骤降，会大大增加内外层混凝土温差。应采取温度控制措施，防止混凝土内外温差引起的温度应力。
1.3混凝土的收缩
混凝土收缩的主要原因是内部水蒸发引起混凝土收缩。干湿交替会引起混凝土体积的交替变化，这对混凝土是很不利的。
2、混凝土裂缝裂缝处理措施
混凝土裂缝的修补措施主要有以下一些方法：表面修补法，灌浆、嵌逢封堵法，结构加固法。混凝土置换法，电化学防护法以及仿生自愈合法。
2.1表面修補法
表面修补法是一种简单、常见的修补方法，它主要适用于稳定和对结构承载能力没有影响的表面裂缝以及深进裂缝的处理。通常的处理措施是在裂缝的表面涂抹水泥浆、环氧胶泥或在混凝土表面涂刷油漆、沥青等防腐材料，在防护的同时为了防止混凝土受各种作用的影响继续开裂，通常可以采用在裂缝的表面粘贴玻璃纤维布等措施。
2.2灌浆、嵌逢封堵法
灌浆法主要适用于对结构整体性有影响或有防渗要求的混凝土裂缝的修补，它是利用压力设备将胶结材料压人混凝土的裂缝中，胶结材料硬化后与混凝土形成一个整体，从而起到封堵加固的目的，常用的胶结材料有水泥浆、环氧树脂、甲基丙烯酸酯、聚氨酯等化学材料。
嵌缝法是裂缝封堵中最常用的一种方法，它通常是沿裂缝凿槽，在槽中嵌填塑性或刚性止水材料，以达到封闭裂缝的目的。常用的塑性材料有聚氯乙烯胶泥、塑料油膏、丁基橡胶等等；常用的刚性止水材料为聚合物水泥砂浆。
2.3结构加固法
当裂缝影响到混凝土结构的性能时，就要考虑采取加固法对混凝土结构进行处理。结构加固中常用的主要有以下几种方法：加大混凝土结构的截面面积。在构件的角部外包型钢、采用预应力法加固、粘贴钢板加固、增设支点加固以及喷射混凝土补强加固。
2.4混凝土置换法
混凝土置换法是处理严重损坏混凝土的一种有效方法，此方法是先将损坏的混凝土剔除，然后再置换人新的混凝土或其他材料。常用的置换材料有：普通混凝土或水泥砂浆、聚合物或改性聚合物混凝土或砂浆。
2.5电化学防护法
电化学防腐是利用施加电场在介质中的电化学作用，改变混凝土或钢筋混凝土所处的环境状态。钝化钢筋，以达到防腐的目的。阴极防护法、氯盐提取法、碱性复原法是化学防护法中常用而有效的三种方法。这种方法的优点是防护方法受环境因素的影响较小，适用钢筋、混凝土的长期防腐，既可用于已裂结构也可用于新建结构。
2.6仿生自愈合法
仿生自愈合法是一种新的裂缝处理方法，它模仿生物组织对受创伤部位自动分泌某种物质，而使创伤部位得到愈合的机能，在混凝土的传统组分中加入某些特殊组分(如含粘结剂的液芯纤维或胶囊)，在混凝土内部形成智能型仿生自愈合神经网络系统，当混凝土出现裂缝时分泌出部分液芯纤维可使裂缝重新愈合。
3、大体积混凝土的配合比设计
3.1水泥的选用
应尽量选用水化热低、凝结时间长的水泥，优先采用中热硅酸盐水泥、低热矿渣硅酸盐水泥、大坝水泥、矿渣硅酸盐水泥、粉煤灰硅酸盐水泥、火山灰质硅酸盐水泥等。
3.2粗细骨料
粗骨料宜采用连续级配，细骨料宜采用中砂。大体积混凝土在保证混凝土强度及坍落度要求的前提下，应提高掺合料及骨料的含量，以降低单方混凝土的水泥用量。
3.3减水剂
为满足和易性和减缓水泥早期水化热发热量的要求，宜在混凝土中掺入适量的缓凝型减水剂。除加入减水剂外，有些混凝土还要根据需要加入其他外加剂，如引气剂、膨胀剂、泵送剂等。
3.4除以上3点外，还要适当降低原材料的温度。
4、浇筑时采取的措施
浇筑方案，除应满足每一处混凝土在初凝以前就被上一层新混凝土覆盖并捣实完毕外，还应考虑结构大小、钢筋疏密、预埋管道和地脚螺栓的留设、混凝土供应情况以及水化热等因素的影响，常用方法有以下2种：
4.1全面分层。即在第一层全面浇筑全部浇筑完毕后，再回头浇筑第二层，此时应使第一层混凝土还未初凝，如此逐层连续浇筑，直至完工为止。采用这种方案，适用于结构平面尺寸一般不宜太大，施工时从短边开始，沿长边推进比较合适。必要时可分成两段，从中间向两端或从两端向中间同时进行浇筑分段分层。混凝土浇筑时，先从底层开始，浇筑至一定距离后浇筑第二层，如此依次向前浇筑其他各层。由于总的层数较多，所以浇筑到顶后，第一层末端的混凝土还未初凝，又可以从第二段依次分层浇筑。这种方案适用于单位时间内要求供应的混凝土较少，结构物厚度不太大而面积或长度较大的工程。
4.2斜面分层。要求斜面的坡度不大于1/3，适用于结构的长度超过厚度3倍的情况。混凝土从浇筑层下端开始，逐渐上移。
5、大体积混凝土养护措施
要尽量长时间保持混凝土湿润状态，避免干缩，使混凝土能够增长强度以抵抗开裂应力。当表面可能干燥很快时，必须连续充分湿润养护以求获得好的表面强度。目前，大体积混凝土常用的养护方法是保温隔热法。采用的表面保温材料包括：保温被、不吸水的泡沫塑料板、聚苯乙烯泡沫塑料板、草袋、砂层保温及喷涂保温层等。在尽量减少混凝土内部温升的前提下，大体积混凝土的养护是一项关键的工作，必须切实做好。
保温的目的主要是为了减少混凝土表面的热扩散，减小混凝土表面的温度梯度，延长散热时间，充分发挥混凝土强度的潜力和材料松弛特性，防止产生表面裂缝。保湿养护的作用是：一是浇筑不久尚处于凝固硬化阶段的混凝土，水化的速度较快，适宜的潮湿条件可防止混凝土表面的脱水而产生收缩裂缝：二是混凝土在保温及潮湿条件下可使水泥的水化作用顺利进行，提高混凝土的抗拉强度。
6、结语
大体积混凝土产生裂缝是由多种原因造成的，在大体积混凝土施工中，合理选择施工材料，优化混凝土配合比，优化混凝土的供应，采用科学的施工方法，严格施工管理，加强大体积混凝土养护，就可以低混凝土温度应力和提高混凝土本身抗拉性能，保证工程质量。