Carbon nitride CN. thin films have been deposited on polycrystalline β-Si3N4 substrates by un-balanced magnetron sputtering in a nitrogen discharge. Both the film deposition rate and the nitrogen concentration decrease with substrate temperature increase in the range of 100~400℃The maximum of nitrogen content is 40 at. pct. Raman spectroscopy and atomic force mi-croscopy were used to characterize the bonding, microstructure and surface roughness of the films. Nanoindentation experiments exhibit a higher hardness of 70 GPa and an extremely elas-tic recovery of 85% at higher substrate temperature.
Carbon nitride CN. Thin films have been deposited on polycrystalline β-Si3N4 substrates by un-balanced magnetron sputtering in a nitrogen discharge. Both the film deposition rate and the nitrogen concentration decrease with substrate temperature increase in the range of 100 ~ 400 ℃ The maximum of nitrogen content is 40 at. pct. Raman spectroscopy and atomic force mi-croscopy were used to characterize the bonding, microstructure and surface roughness of the films. Nanoindentation experiments exhibit a higher hardness of 70 GPa and an extremely elas-tic recovery of 85 % at higher substrate temperature.