钒渣直接合金化工艺的基本方法是将转炉或雾化炉吹炼出的钒渣(含V_2O_515—20％)经过破碎,混入一定量的还原剂(如硅铁、铝等)再加入其它添加剂(如萤石等)制成混合料,在出钢时顺钢流加到钢包内,用电炉生产时还可将钒渣直接加到炉内,完成钒合金化的要求。使用该工艺可省去冶炼钒铁合金的生产工艺,简化流程,节省大量电耗和原材料消耗,还可较大幅度降低钒钢生产成本。据统计,转、平炉钢包内 Vanadium slag direct alloying process is the basic method of converter or atomized furnace blowing vanadium slag (containing V2O515-20%) after crushing, mixed with a certain amount of reductant (such as ferrosilicon, aluminum, etc.) and then add other additives (Such as fluorite, etc.) made of mixture, when the steel flow along the steel added to the ladle, the furnace can also be produced when the vanadium slag added directly to the furnace to complete the vanadium alloy requirements. The process can save the production process of smelting ferrovanadium alloy, simplify the process, save a great deal of power consumption and raw material consumption, and can greatly reduce the vanadium steel production cost. According to statistics, turn, open hearth ladle