The microstructure and wear behaviour of the thermite reaction coating produced by the hybrid laser claddingremelting on AA7075 aluminum alloy for the systems o
【机 构】
：
State Key Laboratory of Plastic Forming Simulation and Mould Technology,State Key Laboratory of Soli
论文部分内容阅读
The microstructure and wear behaviour of the thermite reaction coating produced by the hybrid laser claddingremelting on AA7075 aluminum alloy for the systems of Al-CuO-SiO2, Al-Cr2O3-SiO2, Al-Fe2O3-SiO2, and Al-TiO2-SiO2 were studied. The results of the X-ray diffraction (XRD) analysis show that in all the four reaction coatings, α-Al2O3 and γ-Al2O3 phases were present at the top surface, together with various intermetallic phases, the corresponding reduced metal and Al phase in the fusion zone. Under the dry sliding condition, the wear resistance, in terms of weight loss, of the laser-clad specimens was considerably higher than that of the untreated specimen. The predominant wear mechanism of the former specimens was abrasive wear, while for the latter, it was the adhesive wear that prevailed.
其他文献
Spherical Li(Ni1/3Mn1/3Co1/3)O2 was prepared via the homogenous precursors produced by solution spray-drying method. The precursors were sintered at different t
New layered perovskite compounds, AgxNa2-xLa2Ti3O10 (x=0.2, 0.3 and 0.5) were synthesized by an ion-exchange reaction of Na2La2Ti3O10 with AgNO3 solution and ch
Four types of steel sheets containing 0.04%, 0.09%, 0.14% and 0.36% Si, respectively, were electrodeposited with a nickel layer of 3 μm in thickness and then g
Stable binary single source precursors (SSP) for the deposition of thin films of ceramic semiconductors of composition SnO·GeO were synthesized by close circui
The amorphous Fe78Si9B13 ribbons were bend stress relaxed at various temperature well below the crystallization temperature (Tx) for different time. The effect
Using spark plasma sintering(SPS) technique, TiC particle reinforced γ-TiAl composites were prepared with varying weight fraction of TiC powders. The effects o
Spherical icosahedral quasicrystalline phase (I-phase) was obtained by introducing Ca into Mg-Zn-Y alloy under conventional casting conditions. Due to the addit
研究了非正定方差阵下,证券组合投资模型的最优投资比例系数的计算,有效边界,冗余证券的数量以及套利机会.从而为实证分析提供了理论依据和方法.
This paper studies the ca
A novel carbon-sulfur nano-composite material was synthesized by heating sublimed sulfur and high surface area activated carbon (HSAAC) under certain conditions
The effects of two-stage aging and retrogression and reaging heat treatment on the fracture toughness and stress corrosion cracking resistance of 7475 alloy wer