摘 要:沥青混凝土是以沥青为胶结剂与矿粉、矿物骨料(碎石或砾石和砂料),经过加热、拌和、压实而成的具有一定强度的防渗材料。沥青混凝土配合比设计是根据要求的沥青混凝土的物理力学性质,通过计算和实验来确定组成材料中的碎石、砂、矿粉和沥青之间的合理比例。沥青混凝土的配比选择,首先是按照求最大密实度的原则选择矿料的颗粒级配。沥青混凝土衬砌渠道的成败除了要求正确的设计之外,在很大程度上依赖于施工质量的保证。
关键词:沥青混凝土;现场施工工艺
Abstract: asphalt concrete is asphalt binder ore, mineral aggregate (crushed stone or gravel and sand material), after heating, mixing, compaction made ??with a certain intensity of impermeable material. Asphalt concrete mix design according to the requirements of the physical and mechanical properties of the asphalt concrete calculation and experiment to determine a reasonable proportion between the constituent materials of gravel, sand, slag and asphalt.Asphalt concrete composition choice, first selected in accordance with the principle of seeking maximum density of the particle size distribution of the mineral aggregate. The success or failure of the asphalt concrete lining channels In addition to the requirements of the correct design, to a large extent dependent on the construction quality assurance.
Keywords: asphalt concrete; site construction process
1.准备工作
1.1渠床的整平和压实
渠道土方工程开挖完毕之后,在渠床表面上需加整平。对于一般渠道,密实的沥青混凝土防渗层小于6厘米时,为防止杂草生长,在有条件的地方可用5%的氯化钠溶液喷洒于土壤中,并进行压实。在土基渠床上,若不设垫层时,每平米可用稀释沥青1公斤喷洒一层,进行压实使土壤固结。
1.2材料准备
沥青混合料所用的材料包括沥青、砂、石料、矿粉等。这些材料有的预先加工后运到工地,有的是在制备沥青混合料的地点加工。一般的情况是:砂、石料及矿粉是在料源产地加工;沥青则是在生产沥青混合料的地点加工。
这些材料应按照设计要求准备,沥青在沥青锅中配制合格后,存入专供拌合沥青混合料使用的沥青保温锅中;砂、石料等应分别妥善保存,勿使杂质混入。
2.沥青混合料的拌合
沥青混合料的拌合是将砂、石、矿粉与沥青材料在一定温度下,按照设计比例混合均匀。大体经过材料的配合、烘干、加热、搅拌等几个工序。
2.1拌制沥青混合料应严格按照设计配合比例以重量进行配料。称量的偏差,一般应不超过以下表规定的数值。
2.2各种材料加热、拌和的温度一般参照如下规定的数值进行控制。
2.3沥青混合料的拌和可采用机械拌和或人工拌和的方法。
3.沥青混合料的运输和摊铺
运输的工具视条件而定。要求在运输途中不使沥青混合料的温度降低至摊铺后压实所要求的温度。其温度控制标准如下表里,一般当气温在5℃一下和雨天应停止沥青混合料的铺筑施工。
摊铺混合料以前,要进行必要的放样工作,实地画出摊铺地带的宽度,定出垂直标高。松料摊铺厚度应使铺砌层在压实后能达到设计要求的厚度。沥青混合料的压实系数是1.25~130。
4.沥青混合料摊铺层的压实
在机械力量的作用下使沥青混合料的矿质粒料挤进,细粒料填充较大粒料之间的空隙,同时排出一部分空气,重新分布某些游离沥青,以填充沥青混合料的空隙,从而减小沥青混凝土的孔隙度,达到密实的防渗层。
沥青混凝土的碾压工作必须在混合料摊铺以后(温度合适时)立即进行,并连续碾压,直至沥青混凝土表面上看不见碾子的痕迹时为止。
5.覆盖层的施工,按照设计要求设计覆盖层
预制安装的施工方法 采用预制沥青混凝土构件法的优点是可以工厂化生产,质量容易保证,不妥施工季节和气候的影响,施工机具可以大大简化,同时还可以缩短工期,节约投资。但预制安装的施工接缝多,如处理不好,容易开裂,生长杂草,降低防渗效果。
关键词:沥青混凝土;现场施工工艺
Abstract: asphalt concrete is asphalt binder ore, mineral aggregate (crushed stone or gravel and sand material), after heating, mixing, compaction made ??with a certain intensity of impermeable material. Asphalt concrete mix design according to the requirements of the physical and mechanical properties of the asphalt concrete calculation and experiment to determine a reasonable proportion between the constituent materials of gravel, sand, slag and asphalt.Asphalt concrete composition choice, first selected in accordance with the principle of seeking maximum density of the particle size distribution of the mineral aggregate. The success or failure of the asphalt concrete lining channels In addition to the requirements of the correct design, to a large extent dependent on the construction quality assurance.
Keywords: asphalt concrete; site construction process
1.准备工作
1.1渠床的整平和压实
渠道土方工程开挖完毕之后,在渠床表面上需加整平。对于一般渠道,密实的沥青混凝土防渗层小于6厘米时,为防止杂草生长,在有条件的地方可用5%的氯化钠溶液喷洒于土壤中,并进行压实。在土基渠床上,若不设垫层时,每平米可用稀释沥青1公斤喷洒一层,进行压实使土壤固结。
1.2材料准备
沥青混合料所用的材料包括沥青、砂、石料、矿粉等。这些材料有的预先加工后运到工地,有的是在制备沥青混合料的地点加工。一般的情况是:砂、石料及矿粉是在料源产地加工;沥青则是在生产沥青混合料的地点加工。
这些材料应按照设计要求准备,沥青在沥青锅中配制合格后,存入专供拌合沥青混合料使用的沥青保温锅中;砂、石料等应分别妥善保存,勿使杂质混入。
2.沥青混合料的拌合
沥青混合料的拌合是将砂、石、矿粉与沥青材料在一定温度下,按照设计比例混合均匀。大体经过材料的配合、烘干、加热、搅拌等几个工序。
2.1拌制沥青混合料应严格按照设计配合比例以重量进行配料。称量的偏差,一般应不超过以下表规定的数值。
2.2各种材料加热、拌和的温度一般参照如下规定的数值进行控制。
2.3沥青混合料的拌和可采用机械拌和或人工拌和的方法。
3.沥青混合料的运输和摊铺
运输的工具视条件而定。要求在运输途中不使沥青混合料的温度降低至摊铺后压实所要求的温度。其温度控制标准如下表里,一般当气温在5℃一下和雨天应停止沥青混合料的铺筑施工。
摊铺混合料以前,要进行必要的放样工作,实地画出摊铺地带的宽度,定出垂直标高。松料摊铺厚度应使铺砌层在压实后能达到设计要求的厚度。沥青混合料的压实系数是1.25~130。
4.沥青混合料摊铺层的压实
在机械力量的作用下使沥青混合料的矿质粒料挤进,细粒料填充较大粒料之间的空隙,同时排出一部分空气,重新分布某些游离沥青,以填充沥青混合料的空隙,从而减小沥青混凝土的孔隙度,达到密实的防渗层。
沥青混凝土的碾压工作必须在混合料摊铺以后(温度合适时)立即进行,并连续碾压,直至沥青混凝土表面上看不见碾子的痕迹时为止。
5.覆盖层的施工,按照设计要求设计覆盖层
预制安装的施工方法 采用预制沥青混凝土构件法的优点是可以工厂化生产,质量容易保证,不妥施工季节和气候的影响,施工机具可以大大简化,同时还可以缩短工期,节约投资。但预制安装的施工接缝多,如处理不好,容易开裂,生长杂草,降低防渗效果。