论文部分内容阅读
本文用扫描电镜(SEM)下的单面缺口拉伸试验,考察了Al/SiCp试样的空穴的生成,裂纹的扩展以及裂纹前端微断裂区,指出该材料变脆的原因是由于微断裂区中的一次空穴所造成的.
In this paper, single-sided notched tensile test under scanning electron microscope (SEM) was used to investigate the formation of cavities, the propagation of cracks and the front-end micro-fracture zone in Al / SiCp samples. It is pointed out that the reason of the brittleness is that micro- A hole in the area caused by.