【摘 要】
：
研究了甲基丙烯酸丁酯和苯乙烯两种不同极性单体的原子转移自由基嵌段共聚和无规共聚，得到了实测分子量与理论分子量相近、分子量分布较窄的嵌段共聚物和无规共聚物。聚合过程
论文部分内容阅读
研究了甲基丙烯酸丁酯和苯乙烯两种不同极性单体的原子转移自由基嵌段共聚和无规共聚，得到了实测分子量与理论分子量相近、分子量分布较窄的嵌段共聚物和无规共聚物。聚合过程中分子量和单体转化率成比例增加，多分散性指数变化不大。用１ＨＮＭＲ法测定共聚组成，Ｋｅｌｅｎ－Ｔｕｄｏｓ法计算竞聚率。得到γＳ＝０．９１，γＢＭＡ＝０．３２。
Atom transfer radical block copolymerization and random copolymerization of two kinds of monomers with different polarities, such as butyl methacrylate and styrene, were studied. The results showed that the block copolymers with similar molecular weight and theoretical molecular weight and narrower molecular weight distribution Copolymer. In the polymerization process, the molecular weight and the monomer conversion increase proportionally, and the polydispersity index changes little. The copolymer composition was determined by 1HNMR method and the reactivity ratio was calculated by Kelen-Tudos method. ΓS = 0.91 and γBMA = 0.32 were obtained.
其他文献
报道邻香草醛缩乙醇胺与氯化镉形成的配合物的合成,并对其进行了元素分析,IR等项表征,对配体与氯化镉形成的配合物进行了激光倍频效应的测试和X射线单晶结构分析.[CdC_(20)H_
用电阻加热引上法生长了不开裂、全透明的具有倍频性能的铌酸钾锂（ＫＬＮ）晶体。研究了影响晶体开裂的主要因素和晶体生长的稳定性。发现用引上法生长ＫＬＮ晶体时，要得到全透明、不开裂的ＫＬＮ晶
采用间隙元法求解金属圆管在爆炸焊接时的二维弹粘塑性大变形的接触问题，对圆管内包爆炸焊接的全过程作了详细分析，并对某一具体工程问题进行了计算，得到了爆炸焊接所需的最低爆
用偶合参数热力学积分NPT系综法对甲烷和苯常温常压下在无限稀释水溶液中的化学势及亨利常数进行计算机模拟.模拟中采用周期边界条件、优先抽样方法.水的势能采用TIP4P,甲烷
导出了有限变形下含非完美界面两相复合材料的上下界限.在微小变形下,所导出的界限还原成已知的线性情况下的相应结果.数值上预示了非完美界面特性、有限变形对复合材料有效
本文首先给出滞后广义系统解的稳定性概念,然后建立关于滞后时变广义系统稳定性的拉什密辛(Razumikhin)型定理,最后,作为例子,讨论了一类二阶滞后时变广义系统解的稳定性.
用数值模拟方法研究弹丸跨声速绕流的流动特性,数值模拟的出发方程为平均雷诺数的N-S方程,湍流模型采用Baldwin-Lomax模型,数值格式为四阶的MUSCL TVD格式.通过数值模拟研究
采用脉冲激光淀积技术，在（００１）取向的ＳｉＯ２衬底上制备了ＬｉＮｂＯ３薄膜。为了防止淀积过程缺氧，往淀积腔内充入１０～１５Ｐａ的流动氧气，淀积速度０．３～１．０ｎｍ／ｍｉｎ，淀积时间１ｈ，淀积结束后，充入０．６Ｐａ的氧气，在６５０℃保温０．５ｈ。采用ｘ射线衍射和扫描电镜对
采用McGiniss改良膨胀计与SW-1型微位移测量仪,测定了丙烯酸(AA)-丙烯腈(AN)感光共聚合速率;用102-G气相层析仪及1106型元素分析仪对AA-AN感光聚合体系的单体浓度比及共聚物
引言 化合物的理化性质主要由分子的几何结构和电子结构所决定,如何直接从分子结构预测化合物的理化性质已成为近几年来计算机化学的主要研究内容之一.利用拓扑指数与化合物