【摘 要】
：
通过宏微观形貌观察、金相检验、化学成分分析、压缩及硬度测试等方法,对某大型HDPE挤出机推力轴承盘断裂原因进行分析。结果表明:该推力轴承盘与轴承套圈挤压形成的压痕对推
论文部分内容阅读
通过宏微观形貌观察、金相检验、化学成分分析、压缩及硬度测试等方法,对某大型HDPE挤出机推力轴承盘断裂原因进行分析。结果表明:该推力轴承盘与轴承套圈挤压形成的压痕对推力轴承盘表面裂纹的萌生和疲劳断裂影响极大,推力轴承盘在接触疲劳应力的反复作用下,其表面多处萌生裂纹,逐渐形成多源疲劳,然后向内扩展,直至断裂。并提出了相关解决方法。
The causes of rupture of the thrust bearing plate of a large HDPE extruder were analyzed by macro and micro morphological observation, metallographic examination, chemical composition analysis, compression and hardness testing. The results show that the indentation formed by the thrust bearing disk and the bearing ring greatly affects the surface initiation and fatigue fracture of the thrust bearing disk. Under the action of contact fatigue stress, the thrust bearing disk has many initiation cracks , Gradually formed a multi-source fatigue, and then inward expansion until fracture. And put forward the relevant solutions.
其他文献
随着我国载人航天计划的进展，未来的空间实验室（空间站）将要安排实施一系列的航天医学实验研究项目。为此提出了拟在空间站进行的实验研究计划。总的指导思想是在地面通过适当的
研究了12Cr2Ni4A钢渗碳后的中心硬度控制过程,并解决了该控制过程中造成的变形问题。
The control of the hardness of 12Cr2Ni4A steel after carburizing was studied and
通过金相组织分析,研究了不同均匀化温度和保温时间条件下铸态Mg-Gd-Y-Nd-Zr合金的显微组织,分析了均匀化温度和保温时间对铸态合金组织的影响。结果表明,经530℃保温24h均匀
采用有限元软件模拟了不同板厚下,NM500高强薄钢板辊式淬火过程钢板温度、应力及变形变化规律。结果表明,随着板厚的增加,钢板厚度方向温差增大,冷却速度明显下降。钢板长度
对抽油杆用D级35Mn2钢进行了不同工艺的热处理,并进行了磨损试验、冲击试验和弯曲试验和分析。结果表明:改进抽油杆用钢的热处理工艺,可以有效改善抽油杆抵抗磨损变形、冲击
采用DSC、TEM及XRD检测手段,对在不同冷热结合预处理状态下,Fe65Ni1Al5Ga2P8.65B9.6Si3C5.75非晶条带晶化后的纳米晶形成及晶化体积分数进行了分析研究。结果表明:随预退火温
一革命根據地的建立一九二七年國民黨反動派叛賣了革命,他們與帝國主義者和封建主義者結成了同盟,‘背信棄義地向着中國共產黨與中國人民来一個突然的襲擊,生氣蓬勃的中國大
回顾了铝合金的形变、热处理强化的研究现状,从研究内容、研究对象以及研究方法三个方面总结了形变热处理近10年来研究发生的变化,并综合论述了当下最新的研究成果;进一步展
利用光学显微镜对ST12钢板在拉深及再结晶退火后的不同部位显微组织进行了观察。结果表明:ST12钢拉深后,圆角区域的铁素体晶粒发生了拉伸变形,直壁中间区域的组织演变与圆角
房地产业是我国国民经济重要的支柱产业之一,同时又承担着非常重要的社会保障功能。这种二元属性的存在,使得房地产开发尤其是住宅开发行业的发展深受行业政策影响。现行的城