【摘 要】
：
High Nb containing TiAl alloys with nominal composition of Ti-45Al-9(Nb, W, B) were fabricated at different hot pressing temperatures. The experimental results
【机 构】
：
State Key Laboratory for Advanced Metals and Materials,State Key Laboratory of Powder Metallurgy
论文部分内容阅读
High Nb containing TiAl alloys with nominal composition of Ti-45Al-9(Nb, W, B) were fabricated at different hot pressing temperatures. The experimental results show that the microstructure of alloys hot pressed at 1 300 ℃ is inhomogeneous, for lots of particulate substances containing Ti3Al phase and Nb powders dispersed in TiAl phase matrix. At 1 350 ℃, only a few lamellar colonies form and the diffusion of Nb element is incomplete. With the increase of hot pressing temperature, the microstructure will be more homogeneous. However, borides appear at higher sintering temperature. Meanwhile, the microstructure becomes coarse at 1 500 ℃. 1 400 ℃ will be an appropriate hot pressing temperature for reaction synthesis of high Nb containing TiAl alloys consisting of fully lamellar (FL) microstructure with the colony size of 30-80 μm. Nb element dissolves into the Ti-Al matrix by diffusion. Pore nests form in situ after Nb powders diffusion.
其他文献
In order to examine the dependences of tensile properties of a forged Mg-13Li-X alloy on hot-rolling deformation and the underlying mechanisms tensile tests, re
China is quite poor in argent resource. Roughly 80% of this industrial argent is imported every year. In order to improve the situation, we took advantage of ra
High-resolution X-ray diffractometry (HRXRD) was used to assess the quality of 6H-SiC crystals grown by sublimation method. The results show the occurrence of l
Effects of the process parameters, including deformation temperature, punch velocity and extrusion ratio, on the deformation and microstructure characterization
The nanocrystalline Fe82Nb7B10Cu1 soft magnetic ribbons were treated with the mixture gas flow of ammonia and hydrogen at 673 K. The influence of the nitridatio
This paper reports the influence of heat transfer surface treatment on the formation of calcium sulphate deposit during flow boiling heat transfer. The surface
The alternative heating/cooling cycles(thermal fatigue)of K465 superalloy were carried out. The specimens were held at 1 050 ℃ for 300 s, then quenched into 20
The hot rheological forming method was proposed to form the second titanium alloy vane disk. The hot rheological forming process of the TC11 titanium vane disk
LiFePO4 thin films were prepared by sol-gel technique. The phase and surface morphology were characterized by X-ray diffraction and scanning electron microscopy
In order to solve the reserve stability problem of pyrotechnic explosives containing magnesium powder,a coating method named rapid expansion of supercritical fl