摘 要：对工民建施工中墙体裂缝的防治对策的分析研究具有重要现实意义。施工单位和相关工作人员，应通过不断优化工民建施工中墙体的设计、加强墙體混凝土原材料质量和浇筑施工质量的控制，并做好墙体的后期养护工作等防治对策，避免工民建施工中墙体出现裂缝问题，提高工民建的工程质量，促进我国工民建行业的健康、安全发展。
关键词：工民建施工；墙体裂缝；问题；原因；防治对策Abstract: The countermeasures have the important practical significance on prevention of wall cracks in the civil engineering construction. Construction units and related personnel, by design, constantly optimize the wall in civil construction to strengthen the control of wall concrete raw materials quality and construction quality, and do the maintenance work and Countermeasures of the wall, the wall to avoid civil construction to appear in the crack problem, improve the construction project quality, promote the health, safety and development I in the civil engineering industry.
Keywords:Civil construction; wall crack; problems; reasons; Countermeasures
中图分类号：TU74
1 我国工民建施工中发生墙体裂缝问题的原因分析
1.1 工民建工程结构的沉降不均匀
工民建工程结构的沉降不均匀，是发生墙体裂缝问题重要影响因素。工民建工程的建筑结构会因为地基模板刚度不足、土质松软不均、出现较大的构件支撑间距等原因出现不均匀沉降现象，这种不均匀沉降会导致建筑结构无论是内部还是表面都会出现不均匀的拉应力，从而使得工民建工程的墙体出现严重裂缝问题。同时，沉降类墙体裂缝绝大多数都是深进性或贯穿性的裂缝，会对工民建工程的施工质量造成巨大的危害影响。
1.2 温度方面的原因
温度裂缝也是目前我国工民建工程施工中的主要墙体裂缝类型，其形成原因是墙体混凝土的硬化和凝结过程会产生并聚集大量的热量，导致内外温差不断增大，在混凝土表面形成拉应力导致墙体发生开裂。另外，在墙体后期降温时，受基础构建的限制，墙体的内部也会产生拉应力，出现裂缝问题。
1.3 干缩方面的原因
干缩裂缝具有不可逆性，主要发生在工民建墙体施工完成后进行养护管理阶段的后期。其形成原因是随着水泥浆水分的不断蒸发骤减，导致墙体的混凝土结构也不断干缩最后出现裂缝。
1.4 塑性收缩方面的原因
塑性收缩裂缝也是工民建工程墙体裂缝的其中一种裂缝类型，其主要的形成原因是墙体的混凝土因为表面温度不够、水分不足在充分凝结硬化前发生了收缩，从而导致墙体出现裂缝。水塑性收缩裂缝通常出现具有明显季节性，常见于干热或大风天气施工的墙体混凝土工程，其形状表现为中间宽、两端细、中间宽，不互相连贯，长短也各不相同。
2 我国工民建工程施工中墙体裂缝的防治措施
根据上文所提及的工民建施工中墙体裂缝的形成原因，在实际的墙体项目施工过程中，施工企业和相关工作人员可通过以下防治对策，提高墙体工程的施工技术，保证墙体工程的施工质量，减少避免墙体裂缝的出现。
2.1 优化工民建施工中墙体的设计
一是优化墙体混凝土的配合比设计。设计人员应在确保墙体混凝土的易性指标、结构强度指数等符合建设施工标准的基础上，尽量降低水的使用量，优化墙体混凝土的配合比设计，通过“一高、二掺、三低”的科学配合比，配置出低热量、中弹性、高强度、高韧性和高抗拉的混凝土。
二是合理科学设置构造筋。设计人员应重视墙体混凝土构件的结构设计，并合理科学设置构件的强节点、强锚固、最小配筋率和配筋直径等，增强墙体的抗裂、抗拉性能，禁止墙体混凝土薄弱层的出现。
2.2 做好墙体混凝土材料的质量控制工作
2.2.1 加强水泥的质量控制。工民建墙体施工的混凝土通常选用通用的硅酸盐水泥，类型多样，包括了普通硅酸盐水泥、火山灰质硅酸盐水泥、粉煤质硅酸盐水泥、矿渣质硅酸盐水泥、复合性硅酸盐水泥等。由于不同水泥具有不同的性能，因此在水泥的选用时，应选择正规厂家生产的水泥，并确保该水泥的强度等级、技术要求等都符合国家标准。同时，施工单位还要加强对购进水泥的入场验收工作，认真查看水泥的出厂检验单，严格检测水泥的安定性、强度、凝结时间。此外，在水泥的使用过程中，应坚持先到先用原则，避免积压，注意水泥的贮存期不能超过三个月。
2.2.2 加强骨料的质量控制。砂石骨料是混凝土的主要组成成分，其质量好坏对墙体的混凝土强度质量具有直接和重要影响。因此，在选择骨料时，相关工作人员除应考虑价格因素外，还应充分考虑骨料的质量要求，坚持就地取材原则，选择级配良好、含有害杂质少的、不与水泥发生化学反应的天然或人工骨料。
2.2.3 严格控制外加剂的选择。外加剂的选择必须实事求是，根据工程具体的施工工艺、天气条件、混凝土性能、水泥的适应性等科学合理选择外加剂的种类和数量。
2.2.4 加强掺合物质量控制。添加不同的掺和料能够促进新拌混凝土的硬化或强度等性能的改善。因此，必须做好掺和物的分级、分类储存工作，避免污染或受潮。
2.3 加强墙体混凝土浇筑施工的质量控制
墙体混凝土的浇筑施工是工民建工程墙体施工的重点工作，好的施工质量能有效防止墙体出现裂缝。因此在实际浇筑时，必须做好以下注意工作。
2.3.1 降低墙体混凝土的入模温度。方法有：一是在混凝土的拌合水中加入冰屑或地下水进行降温。二是当施工现场天气炎热气温较高时，露天砂石应避免阳光直射，进行草席或幕布的覆盖降温处理，并在使用前利用水的冲洗降低温温。
2.3.2 加强混凝土内部温度的控制。主要方法是在墙体混凝土的内部预设冷却水管，利用冷水的不断循环加速热量的挥发，减少因混凝土冷却凝固导致的热量存在，保证墙体混凝土的易性和结构强度。
2.3.3 把握振捣力度，控制振捣时间。二次机械振捣是墙体混凝土浇筑过程的最常用振捣方式。在实际的二次振捣工作中，必须确保模板等建筑结构的固定不动摇，把握好振捣力度，控制好振捣用时，防止墙体出现微裂或裂缝现象。
2.3.4 坚持分层浇筑。具体的灌筑流程是先对准钢筋笼和钻孔中心，然后加固模板，最后进行混凝土的分层灌筑。
2.3.5 准确设置后浇带。在混凝土浇筑平面过大的情况下，可在设计许可的指导下准确设置后浇带，提高混凝土的散热速度，降低墙体混凝土的拉应力，避免混凝土产生裂缝。
2.4 做好墙体的养护工作
墙体养护是指完成墙体混凝土的灌注工作后，加强墙体湿度和温度的控制，确保墙体混凝土硬化后的易性和强度符合标准，防治出现墙体裂缝。墙体的养护工作具有明显季节特点，一是在炎热高温的夏季，应对墙体混凝土的表层进行敷设，并定期洒水，切实有效做好墙体混凝土表层的降温工作，减小温差，避免墙体的表层发生开裂。二是在寒冷低温的冬季，应对墙体的混凝土表层进行覆盖保温布和塑料膜等保温措施，避免墙体在寒潮的侵袭影响影响下出现裂缝。同时，必须保证墙体混凝土具有适宜的湿度，定期洒水并辅以湿润的草帘和麻袋的覆盖，提高墙体混凝土的防渗性能，避免发生墙体裂缝问题。
3 结束语
综上所述，随着国家社会经济的高速发展，我国的工民建筑事业也得到不断的壮大，取得了良好的成绩。但在实际的工民建筑施工中，也发现了不少问题，其中最为常见的就是墙体裂缝问题。鉴于此，笔者将本文命名为《工民建施工中墙体裂缝的防治对策研究》，首先分析了工民建施工过程中出现墙体裂缝的原因，然后提出相应的防治对策，最后进行总结，旨在加强与同行的沟通交流，减少甚至防止墙体裂缝问题的发生，减少住户投诉，提高我国工民建的施工质量，保障其使用性能，延长其使用寿命。
参考文献
[1]王国权.分析工民建施工中墙体裂缝的防治措施[J].科技创新导报，2012，33：53+55.
[2]孙卫东. 工民建施工中墙体裂缝预防措施 [J]. 现代商贸工业，2013，2：175-176.
[3]邵庆琳.工民建工程施工中墙体质量问题分析 [J].科技创业家，2012，22：68.
[4]熊志力.浅议工民建施工中墙体裂缝的防治措施[J].企业家天地(理论版)，2010，6：32.
关键词：工民建施工；墙体裂缝；问题；原因；防治对策Abstract: The countermeasures have the important practical significance on prevention of wall cracks in the civil engineering construction. Construction units and related personnel, by design, constantly optimize the wall in civil construction to strengthen the control of wall concrete raw materials quality and construction quality, and do the maintenance work and Countermeasures of the wall, the wall to avoid civil construction to appear in the crack problem, improve the construction project quality, promote the health, safety and development I in the civil engineering industry.
Keywords:Civil construction; wall crack; problems; reasons; Countermeasures
中图分类号：TU74
1 我国工民建施工中发生墙体裂缝问题的原因分析
1.1 工民建工程结构的沉降不均匀
工民建工程结构的沉降不均匀，是发生墙体裂缝问题重要影响因素。工民建工程的建筑结构会因为地基模板刚度不足、土质松软不均、出现较大的构件支撑间距等原因出现不均匀沉降现象，这种不均匀沉降会导致建筑结构无论是内部还是表面都会出现不均匀的拉应力，从而使得工民建工程的墙体出现严重裂缝问题。同时，沉降类墙体裂缝绝大多数都是深进性或贯穿性的裂缝，会对工民建工程的施工质量造成巨大的危害影响。
1.2 温度方面的原因
温度裂缝也是目前我国工民建工程施工中的主要墙体裂缝类型，其形成原因是墙体混凝土的硬化和凝结过程会产生并聚集大量的热量，导致内外温差不断增大，在混凝土表面形成拉应力导致墙体发生开裂。另外，在墙体后期降温时，受基础构建的限制，墙体的内部也会产生拉应力，出现裂缝问题。
1.3 干缩方面的原因
干缩裂缝具有不可逆性，主要发生在工民建墙体施工完成后进行养护管理阶段的后期。其形成原因是随着水泥浆水分的不断蒸发骤减，导致墙体的混凝土结构也不断干缩最后出现裂缝。
1.4 塑性收缩方面的原因
塑性收缩裂缝也是工民建工程墙体裂缝的其中一种裂缝类型，其主要的形成原因是墙体的混凝土因为表面温度不够、水分不足在充分凝结硬化前发生了收缩，从而导致墙体出现裂缝。水塑性收缩裂缝通常出现具有明显季节性，常见于干热或大风天气施工的墙体混凝土工程，其形状表现为中间宽、两端细、中间宽，不互相连贯，长短也各不相同。
2 我国工民建工程施工中墙体裂缝的防治措施
根据上文所提及的工民建施工中墙体裂缝的形成原因，在实际的墙体项目施工过程中，施工企业和相关工作人员可通过以下防治对策，提高墙体工程的施工技术，保证墙体工程的施工质量，减少避免墙体裂缝的出现。
2.1 优化工民建施工中墙体的设计
一是优化墙体混凝土的配合比设计。设计人员应在确保墙体混凝土的易性指标、结构强度指数等符合建设施工标准的基础上，尽量降低水的使用量，优化墙体混凝土的配合比设计，通过“一高、二掺、三低”的科学配合比，配置出低热量、中弹性、高强度、高韧性和高抗拉的混凝土。
二是合理科学设置构造筋。设计人员应重视墙体混凝土构件的结构设计，并合理科学设置构件的强节点、强锚固、最小配筋率和配筋直径等，增强墙体的抗裂、抗拉性能，禁止墙体混凝土薄弱层的出现。
2.2 做好墙体混凝土材料的质量控制工作
2.2.1 加强水泥的质量控制。工民建墙体施工的混凝土通常选用通用的硅酸盐水泥，类型多样，包括了普通硅酸盐水泥、火山灰质硅酸盐水泥、粉煤质硅酸盐水泥、矿渣质硅酸盐水泥、复合性硅酸盐水泥等。由于不同水泥具有不同的性能，因此在水泥的选用时，应选择正规厂家生产的水泥，并确保该水泥的强度等级、技术要求等都符合国家标准。同时，施工单位还要加强对购进水泥的入场验收工作，认真查看水泥的出厂检验单，严格检测水泥的安定性、强度、凝结时间。此外，在水泥的使用过程中，应坚持先到先用原则，避免积压，注意水泥的贮存期不能超过三个月。
2.2.2 加强骨料的质量控制。砂石骨料是混凝土的主要组成成分，其质量好坏对墙体的混凝土强度质量具有直接和重要影响。因此，在选择骨料时，相关工作人员除应考虑价格因素外，还应充分考虑骨料的质量要求，坚持就地取材原则，选择级配良好、含有害杂质少的、不与水泥发生化学反应的天然或人工骨料。
2.2.3 严格控制外加剂的选择。外加剂的选择必须实事求是，根据工程具体的施工工艺、天气条件、混凝土性能、水泥的适应性等科学合理选择外加剂的种类和数量。
2.2.4 加强掺合物质量控制。添加不同的掺和料能够促进新拌混凝土的硬化或强度等性能的改善。因此，必须做好掺和物的分级、分类储存工作，避免污染或受潮。
2.3 加强墙体混凝土浇筑施工的质量控制
墙体混凝土的浇筑施工是工民建工程墙体施工的重点工作，好的施工质量能有效防止墙体出现裂缝。因此在实际浇筑时，必须做好以下注意工作。
2.3.1 降低墙体混凝土的入模温度。方法有：一是在混凝土的拌合水中加入冰屑或地下水进行降温。二是当施工现场天气炎热气温较高时，露天砂石应避免阳光直射，进行草席或幕布的覆盖降温处理，并在使用前利用水的冲洗降低温温。
2.3.2 加强混凝土内部温度的控制。主要方法是在墙体混凝土的内部预设冷却水管，利用冷水的不断循环加速热量的挥发，减少因混凝土冷却凝固导致的热量存在，保证墙体混凝土的易性和结构强度。
2.3.3 把握振捣力度，控制振捣时间。二次机械振捣是墙体混凝土浇筑过程的最常用振捣方式。在实际的二次振捣工作中，必须确保模板等建筑结构的固定不动摇，把握好振捣力度，控制好振捣用时，防止墙体出现微裂或裂缝现象。
2.3.4 坚持分层浇筑。具体的灌筑流程是先对准钢筋笼和钻孔中心，然后加固模板，最后进行混凝土的分层灌筑。
2.3.5 准确设置后浇带。在混凝土浇筑平面过大的情况下，可在设计许可的指导下准确设置后浇带，提高混凝土的散热速度，降低墙体混凝土的拉应力，避免混凝土产生裂缝。
2.4 做好墙体的养护工作
墙体养护是指完成墙体混凝土的灌注工作后，加强墙体湿度和温度的控制，确保墙体混凝土硬化后的易性和强度符合标准，防治出现墙体裂缝。墙体的养护工作具有明显季节特点，一是在炎热高温的夏季，应对墙体混凝土的表层进行敷设，并定期洒水，切实有效做好墙体混凝土表层的降温工作，减小温差，避免墙体的表层发生开裂。二是在寒冷低温的冬季，应对墙体的混凝土表层进行覆盖保温布和塑料膜等保温措施，避免墙体在寒潮的侵袭影响影响下出现裂缝。同时，必须保证墙体混凝土具有适宜的湿度，定期洒水并辅以湿润的草帘和麻袋的覆盖，提高墙体混凝土的防渗性能，避免发生墙体裂缝问题。
3 结束语
综上所述，随着国家社会经济的高速发展，我国的工民建筑事业也得到不断的壮大，取得了良好的成绩。但在实际的工民建筑施工中，也发现了不少问题，其中最为常见的就是墙体裂缝问题。鉴于此，笔者将本文命名为《工民建施工中墙体裂缝的防治对策研究》，首先分析了工民建施工过程中出现墙体裂缝的原因，然后提出相应的防治对策，最后进行总结，旨在加强与同行的沟通交流，减少甚至防止墙体裂缝问题的发生，减少住户投诉，提高我国工民建的施工质量，保障其使用性能，延长其使用寿命。
参考文献
[1]王国权.分析工民建施工中墙体裂缝的防治措施[J].科技创新导报，2012，33：53+55.
[2]孙卫东. 工民建施工中墙体裂缝预防措施 [J]. 现代商贸工业，2013，2：175-176.
[3]邵庆琳.工民建工程施工中墙体质量问题分析 [J].科技创业家，2012，22：68.
[4]熊志力.浅议工民建施工中墙体裂缝的防治措施[J].企业家天地(理论版)，2010，6：32.