【摘 要】
：
针对高炉炉渣中Al2O3含量(质量分数)偏高导致炉渣黏度增大、 流动性变差、 脱硫能力下降的问题,利用双层石墨坩埚模拟铁液滴下穿过炉渣的过程,探究了R[w(CaO)/w(SiO2)],w(MgO)/w(Al2O3)和w(Al2O3)对高Al2O3型CaO-SiO2-MgO-Al2O3四元高炉渣系脱硫能力的影响.当w(MgO)/w(Al2O3)=0.50,w(Al2O3)=20％时,R由1.05提高到1.35,炉渣的脱硫能力增强;当w(Al2O3)=20％,R=1.30时,w(MgO)/w(Al2O3)由0
【机 构】
：
东北大学 冶金学院,沈阳 110819;河钢集团 宣钢公司,河北 张家口 075100
论文部分内容阅读
针对高炉炉渣中Al2O3含量(质量分数)偏高导致炉渣黏度增大、 流动性变差、 脱硫能力下降的问题,利用双层石墨坩埚模拟铁液滴下穿过炉渣的过程,探究了R[w(CaO)/w(SiO2)],w(MgO)/w(Al2O3)和w(Al2O3)对高Al2O3型CaO-SiO2-MgO-Al2O3四元高炉渣系脱硫能力的影响.当w(MgO)/w(Al2O3)=0.50,w(Al2O3)=20％时,R由1.05提高到1.35,炉渣的脱硫能力增强;当w(Al2O3)=20％,R=1.30时,w(MgO)/w(Al2O3)由0.25提高到0.55,炉渣的脱硫能力增强;当w(MgO)/w(Al2O3)=0.40,R=1.30时,w(Al2O3)由12％提高到20％,炉渣的脱硫能力下降.
其他文献
To reduce electromagnetic (EM) wave interference pollution,in this work,carbon fibers@Co-ZIFs deriva-tions (CFZD) as an advanced EM wave absorbing material was successfully prepared.The yolk-shell struc-ture of the magnetic metal particles generated a lar
A combination of both conventional and advanced high-resolution characterization techniques was ap-plied to study the modified layers on the surface of three composite Al-Cr arc cathodes with identical nominal composition of Al-50 at.％ Cr but varying powd
以传统的理论燃烧温度模型为基础,建立了高炉富氢燃料喷吹的新理论燃烧温度模型.基于某厂1号高炉的实际生产数据,验证了模型的准确性和可靠性.研究结果表明,富氢高炉理论燃烧温度新模型预测结果与高炉实测数据吻合良好.新模型以合理的理论燃烧温度范围为基准,分别获得了富氧率(fO)、煤比(MPCI)、天然气喷吹量(VNG)等参数与理论燃烧温度(tf)间的关系,同时还分析了3个操作参数间的合理匹配问题.新模型获得的参数匹配规律可以为不同企业的高炉在复合喷吹煤粉与天然气时实现稳定运行提供一定的参考依据.
炼钢过程主要是通过喷吹手段来达到脱碳、 脱磷、 脱硫、 去夹杂等冶金目的,其过程涉及极其复杂的气-金-渣多相流行为和反应动力学,对其研究揭示是实现高效炼钢和钢超洁净化的重要基础,数值模拟已成为解析炼钢过程现象和机理不可或缺的手段.本文结合前人的工作,总结介绍了作者在转炉冶炼和钢包精炼过程数值模拟方面的研究进展.通过对转炉冶炼熔池内渣-金-气多相流行为的数值模拟,揭示了熔池混匀、炉衬冲刷、金属液滴喷溅等重要物理现象,同时通过耦合冶金热力学,定量描述了转炉内脱碳、脱磷等反应过程,优化了转炉吹炼工艺;基于Eul
Nanodiamonds (NDs) were prepared under ambient pressure by sublimation decomposition of silicon carbide in an intermediate frequency furnace for only 8 min.The synthesis proceeded in the temperature range of 2600-2800 ℃ without any catalyst or highly acti
Surgical prostheses and implants used in hard-tissue engineering should satisfy all the clinical,mechani-cal,manufacturing,and economic requirements in order to be used for load-bearing applications.Metals,and to a lesser extent,polymers are promising mat
In the current work,a parallel comparison of the influence of Al,Mo and Ti,on the microstructure and strengthening of the CoCrFeNi alloy was conducted.To achieve this,inconsistencies on variables includ-ing the extent of alloying,thermomechanical processi
采用热力学平衡实验,结合SEM-EDS等检测方法,确定了空气气氛条件下CaO-Al2O3-CeO2渣系在1500℃的相平衡关系,并绘制出该渣系的等温相图.在空气气氛条件下,CaO-Al2O3-CeO2渣系在1500℃时存在着三种三相平衡(CA+CA2+CeO2,L+CaO+CeO2,L+CA+CeO2)和两种两相平衡(L+CeO2,L+CaO),根据各平衡相关系划分了相应相区,且CeO2在该渣系中的最大溶解度为28％(质量分数).
研究了转炉放散炉气在竖炉中预热废钢的传热规律,建立了废钢多孔介质中的瞬态非热平衡流固耦合模型;通过FLUENT模拟得出废钢传热特性曲线和废钢料层内部的温度分布,分析了废钢预热中料层高度、转炉放散炉气温度和进气速度对废钢温度及预热效率的影响.研究结果表明:在1200℃炉气中,废钢经30 min预热后温度达到570.3℃,预热效率为38.3％;随着废钢料层高度从2.5 m降低到0.7 m,废钢温度从570.3℃升高到695.7℃,预热效率下降为13.3％;随着转炉放散炉气温度从1200℃升高到1600℃,废钢
为了实现脱磷钢渣中P2O5的选择性浸出,研究了不同Fe2O3质量分数的脱磷钢渣在不同pH值下的浸出行为.研究结果表明:提高渣中Fe2O3质量分数有利于促进P2O5在固溶体中的富集,并且能促进磷的浸出和抑制铁的浸出;脱磷钢渣中磷的浸出率远高于铁.随着pH值的降低,磷和铁的浸出率都升高;在pH=5时,高Fe2O3质量分数的脱磷钢渣中磷的浸出率达到85.8％,而铁的浸出率只有2.8％,实现了磷和铁的有效分离;酸浸后的残渣C中Fe2O3质量分数高达59.1％,而P质量分数仅为0.29％,且含有Ca和Mg等有益元素