Thermal explosion method was used to prepare porous NiTi shape memory alloy. The process of thermal explosion was investigated. The effect of process parameters on thermal explosion reaction and properties of products was analyzed. The results showed heating rate, green density, particle size of initial powder strongly affected combustion temperature, porosity and compressive strength of final products. The mechanism of thermal explosion and the microstructure of reacted products were studied by XRD and SEM photographs. The results showed the final products mainly comprised of NiTi, Ti2Ni and TiNi3 phases and their strength decreased with the increase of porosity.
The process of thermal explosion was investigated. The effect of process parameters on thermal explosion reaction and properties of products was analyzed. The results showed heat rate, green density, particle size of initial powder strongly affected combustion temperature, porosity and compressive strength of final products. The mechanism of thermal explosion and the microstructure of reacted products were studied by XRD and SEM photographs. The results showed the final products are mainly composed of NiTi, Ti2Ni and TiNi3 phases and their strength decreased with the increase of porosity.