【摘 要】
：
采用丙烯酸酯原位聚合物增韧改性多官能环氧树脂,制备了J-241室温固化耐150℃结构胶黏剂。研究了胶黏剂的对金属材料和环氧碳纤维复合材料的粘接性能。制备的胶黏剂具有良好
【机 构】
：
黑龙江省科学院石油化学研究院,黑龙江省科学院高技术研究院,
论文部分内容阅读
采用丙烯酸酯原位聚合物增韧改性多官能环氧树脂,制备了J-241室温固化耐150℃结构胶黏剂。研究了胶黏剂的对金属材料和环氧碳纤维复合材料的粘接性能。制备的胶黏剂具有良好的室温固化性能,固化后室温剪切强度33.2MPa、150℃剪切强度13.6MPa,剥离强度35.2N/cm,对环氧碳纤维复合材料具有良好的粘接性能,可用于环氧碳纤维复合材料结构的修补和二次连接成型。
Acrylate in-situ polymer toughening modified polyfunctional epoxy resin, prepared J-241 room temperature curing 150 ℃ structural adhesive. The adhesion properties of the adhesive to the metal material and the epoxy carbon fiber composite material were studied. The prepared adhesive has good curing property at room temperature, after curing, the shear strength at room temperature is 33.2MPa, the shear strength at 150 ℃ is 13.6MPa and the peel strength is 35.2N / cm, which has good adhesive property to the epoxy carbon fiber composite material. Epoxy carbon fiber composite structure repair and secondary connection molding.
其他文献
In this study,the limit state equation for tensile reliability analysis of the foundation surface of a gravity dam was established.The possible crack length was
以磷酸盐料浆、空心微珠与空心石英纤维为主要原材料,采用铺层法制备了一种承载/隔热一体的复合材料。并采用热重法(TG)测试了磷酸盐基浆料和石英纤维1000℃失重;用扫描电子
胺碘酮作为抗心律失常药物,于70年代末在我国开始应用于临床.有关这个药物的临床研究在各地广泛开展起来,比如:维持窦性心律,防治心肌梗死后心律失常,以及延长充血性心力衰竭
探索了聚醋酸乙烯乳液合成过程中各组分(如引发剂、乳化剂、增塑剂)对其粘接强度的影响,以期优化乳液聚合的配方,提高聚醋酸乙烯酯乳液的黏合力。通过研究发现,对压剪强度的
以2,4-甲苯二异氰酸酯、甲基丙烯酸羟丙酯和E-03环氧树脂为原料合成了异氰酸酯化丙烯酸酯大单体,用其作为官能单体,同丙烯酸酯软硬单体在引发剂的作用下,以环氧树脂为分散介
在混凝土预制厂中制作挡土墙时,对自密实混凝土(简称SCC)和高性能混凝土(简称HPC)进行了比较,试验表明,SCC某种情况下可以替代HPC.在试验室中进行的性能研究,包括材料的微观
钆贝葡胺是一种非特异性细胞外间隙对比剂，具有高弛豫率和肾脏、胆道双重排泄的特点。目前对国内儿童钆贝葡胺的临床应用尚缺乏统一的认识。经中华医学会放射学分会儿科学组、中华医学会儿科学分会放射学组多名儿科影像专家反复讨论，以翔实的文献为依据，结合临床应用经验，对钆贝葡胺的理化特性、药代动力学特点、儿童中枢神经系统增强检查临床应用及安全性等达成共识。钆贝葡胺禁用于钆对比剂过敏的患者。由于钆贝葡胺能在显著缩
对比分析了基于场地观测数据模拟的和FY-3A中分辨率光谱成像仪(MERSI)红外通道星上定标观测卫星入瞳亮温值。主要的场地观测数据来自于2008、2009年青海湖以及2010年敦煌外场