Effects of Chromium Addition on Preparation and Properties of Bulk Cementite

来源 :Journal of Iron and Steel Research(International) | 被引量 : 0次 | 上传用户:haose1989
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Bulk cementites with the Cr contents of 0,3.01,6.03,8.22,and 11.51mass% were prepared by mechanical alloying(MA)and spark plasma sintering(SPS).The results indicated that when the Cr content was low(3.01mass%),the phases were composed of cementite with a small amount ofα-Fe at a sintering temperature of 1 173 K,but the microstructure became single-phase alloyed cementite as the Cr content was further increased.It showed that microaddition of Cr was beneficial for promoting the formation of cementite.Furthermore,the mechanical performance of cementite can be greatly affected by the variation of Cr content.The hardness,elastic modulus and elastic recovery presented a remarkably increasing tendency with the addition of Cr,and the maximum micro-hardness and elastic modulus values reached 1 070.74 HV and 199.32 GPa,respectively,which were similar to the precipitation phase(cementite)obtained by melting and casting techniques.Moreover,when the Cr content was below 11.51mass%,the crystal structure of Fe_3C-type cementite would not change with increasing the Cr content.A Cr atom replaced an Fe atom in the lattice of the cementite,and voids appeared when Cr was doped into the cementite at content of about11.51mass%,causing the relative density to decrease. Bulk cementites with the Cr contents of 0, 3.01, 6.03, 8.22, and 11.51 mass% were prepared by mechanical alloying (MA) and spark plasma sintering (SPS). The results indicated that when the the Cr content was low (3.01 mass% , the phases were composed of cementite with a small amount of α-Fe at a sintering temperature of 1 173 K, but the microstructure became single-phase alloyed cementite as the Cr content was further increased .It showed that microaddition of Cr was beneficial for promoting the formation of cementite. Fermentmore, the mechanical performance of cementite can greatly affected by the variation of Cr content. hardness, elastic modulus and elastic recovery presented a remarkably increasing tendency with the addition of Cr, and the maximum micro-hardness and elastic modulus values ​​reached 1 070.74 HV and 199.32 GPa, respectively, which were similar to the precipitation phase (cementite) obtained by melting and casting techniques. Moreover, when the Cr content was below 11.51 mass%, the crystal str ucture of Fe_3C-type cementite would not change with increasing the Cr content. A Cr atom replaced an Fe atom in the lattice of the cementite, and voids had when Cr was doped into the cementite at content of about11.51mass%, causing the relative density to decrease.
其他文献
To achieve ultrasonic casting of 35 CrMo steel,the waveguide unit for introducing ultrasound into liquid steel was studied numerically and experimentally.The st
The knowledge of transient temperature of the ladle wall is a key factor in optimizing energy consumption in steelmaking process.The transient temperature needs
To develop a high-efficiency desulfurizer for the production of pipeline steel with the LD-RH-CC process,the desulfurization efficiency and mechanism of CaO-sat
Obtaining small carbides is crucial but difficult for high-speed steels.A new approach for refining carbide dimensions in M42 super hard high-speed steel by inc
Cable-type welding wire(CWW)CO_2 welding is an innovative process arc welding with high quality,high efficiency and energy saving,in which CWW is used as consum
Total 72 lapped specimens including six different kinds of CR340 steel structures were prepared to study the influence of the spot welding technology on their f
One assumption underlying the conventional dilatometric analysis based on the lever rule is that the volume of the specimen changes isotropically during phase t
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
简述了对压缩机长周期稳定运行所采取的几项措施及效益。 The measures and benefits of compressor long-term stable operation are briefly described.
The arc spraying technique was adopted to prepare three types of iron-based coatings including 08Mn2 Si,4Cr13,and 65 Mn.Meanwhile,the metallurgical microscope a