Arc spraying coatings are widely used in various applications, but uncommon in cast iron substrate. Different surface pretreatment technology is tested on substrates of gray cast iron. Surface roughness and residual stress were measured by TR200 and X-ray diffraction analyzer. Influence of different surface pretreatment methods ( dry blasting and fusebond) on roughness and residual stress was analyzed. The arc-sprayed coatings of wire 3Cr13 (φ2mm) on gray cast iron substrate is studied. The microstructure and interface of bonding layer were observed by SEM. The bond strength was taken by tensile test. Results show that bond strength with grit blasting is higher than fuse-bond; it is feasible to make wire 3Cr13 coating with arc spraying on cast iron substrate roughened by grit blasting.